Use of ceramics in dental and orthodontic applications

ABSTRACT

The invention relates to uses of glasses and glass-ceramics in dental and orthodontic applications.

CROSS REFERENCE TO RELATED APPLICATION

This application is a divisional of U.S. application Ser. No. 10/358,856, filed Feb. 5, 2003, now allowed, the disclosure of which is herein incorporated by reference.

BACKGROUND

The invention relates to uses of ceramics in dental and orthodontic applications.

Although performance and durability are highly desirable characteristics for dental replacement and repair work, for example, they alone are not the sole concern for practitioners and patients. Aesthetic value, or how dental materials and articles and orthodontic appliances look inside the mouth is just as desirable.

For example, in prosthodontics and restorative dentistry, where tooth replacement or prostheses are custom made to fit in or on a tooth structure, there are instances where the restoration or repair can be seen from a short distance when the mouth is open. Thus in those instances, it would be highly desired that the dental material be nearly indistinguishable from adjacent tooth structure.

Prosthetics and restorative dentistry encompass the fabrication and installation of, for example, restoratives, replacements, inlays, onlays, veneers, full and partial crowns, bridges, implants, and posts. Conventional materials used to make dental prostheses include gold, ceramics, amalgam, porcelain, and composites. In terms of aesthetic value, it is perceived that porcelains, composites, and ceramics look better than amalgam and metals, since a prosthetic made from those nonmetals better matches or blends in with the color of adjacent natural teeth.

For orthodontic appliances (typically, brackets, which are small slotted bodies for holding a curved arch wire, and associated tooth bands if banded attachment is used), stainless steel is an ideal material because it is strong, nonabsorbent, weldable, and relatively easy to form and machine. A significant drawback of metal appliances, however, relates to cosmetic appearance when the patient smiles. Adults and older children undergoing orthodontic treatment are often embarrassed by the “metallic smile” appearance of metal bands and brackets, and this problem has led to various improvements in recent years.

One area of improvement involves use of nonmetal materials. Both plastic and ceramic materials present an improved appearance in the mouth, and often the only significantly visible metal components are thin arch wires that are cosmetically acceptable. Plastic is not an ideal material because it lacks the structural strength of metal, and is susceptible to staining and other problems. Ceramics such as sapphire or other transparent crystalline materials have undesirable prismatic effects. Also, single crystal aluminum oxide appliances are subject to cleavage under the loads that occur in the course of orthodontic treatment. Other ceramics have been largely opaque so that they either do not match tooth color or require coloring.

Glasses and glass-ceramics have also been used for dental replacement and repair work. Sinterable glass-ceramics based on lithium disilicate utilized in production of shaped dental products are known. For example, some compositions are based on SiO₂ (57-80 wt-%) and Li₂O (11-19 wt-%) with minor amounts of Al₂O₃, La₂O₃, MgO, ZnO, K₂O, P₂O₅ and other materials. Another examples are moldable ceramic-glass compositions which include 50-99 parts by weight of alumina and/or zirconia powder and 1 to 50 parts by weight of glass powder.

Digitized machining of ceramics (commonly known as CAD/CAM milling) is one method for producing useful dental shapes. However, the machining of fully densified structural ceramics like Al₂O₃ and ZrO₂ into complex dental geometries is difficult due to rapid tool wear. For this reason, methods involving machining of green ceramic body have been developed (e.g. LAVA ZrO₂ by 3M Company).

SUMMARY

In one embodiment, the invention provides an article comprising a ceramic in the form of a dental article or an orthodontic appliance wherein the ceramic comprises at least one of a ceramic, glass, or glass-ceramic comprising:

-   -   a) at least 35 percent by weight Al₂O₃, based on the total         weight of the glass or glass-ceramic, and a first metal oxide         other than Al₂O₃, wherein the glass or glass-ceramic contains         not more than 10 percent by weight collectively B₂O₃, GeO₂,         P₂O₅, SiO₂, TeO₂, and V₂O₅, based on the total weight of the         glass or glass-ceramic;     -   b) at least 35 percent by weight Al₂O₃, based on the total         weight of the glass or glass-ceramic, and a first metal oxide         other than Al₂O₃, wherein the Al₂O₃ and the first metal oxide         collectively comprise at least 70 percent by weight of the glass         or glass-ceramic;     -   c) Al₂O₃ and at least one of REO or Y₂O₃, wherein at least 80         percent by weight of the glass or glass-ceramic collectively         comprises the Al₂O₃ and the at least one of REO or Y₂O₃, based         on the total weight of the glass or glass-ceramic;     -   d) Al₂O₃, at least one of REO or Y₂O₃, and at least one of ZrO₂         or HfO₂, wherein at least 80 percent by weight of the glass or         glass-ceramic collectively comprises the Al₂O₃, at least one of         REO or Y₂O₃, and at least one of ZrO₂ or HfO₂, based on the         total weight of the glass or glass-ceramic;     -   e) Al₂O₃ and at least one of REO or Y₂O₃, wherein at least 60         percent by weight of the glass or glass-ceramic collectively         comprises the Al₂O₃ and the at least one of REO or Y₂O₃, and         wherein the glass or glass-ceramic contains not more than 20         percent by weight SiO₂ and not more than 20 percent by weight         B₂O₃, based on the total weight of the glass or glass-ceramic;     -   f) Al₂O₃, at least one of REO or Y₂O₃, and at least one of ZrO₂         or HfO₂, wherein at least 60 percent by weight of the glass or         glass-ceramic collectively comprises the Al₂O₃, at least one of         REO or Y₂O₃, and at least one of ZrO₂ or HfO₂, and wherein the         glass or glass-ceramic contains not more than 20 percent by         weight SiO₂ and not more than 20 percent by weight B₂O₃, based         on the total weight of the glass or glass-ceramic;     -   g) Al₂O₃ and at least one of REO or Y₂O₃, wherein at least 60         percent by weight of the glass or glass-ceramic comprise the         Al₂O₃ and the at least one of REO or Y₂O₃, and wherein the glass         or glass-ceramic contains not more than 40 percent by weight         collectively SiO₂, B₂O₃, and P₂O₅, based on the total weight of         the glass or glass-ceramic;     -   h) Al₂O₃, at least one of REO or Y₂O₃, and at least one of ZrO₂         or HfO₂, wherein at least 60 percent by weight of the glass or         glass-ceramic collectively comprises the Al₂O₃, at least one of         REO or Y₂O₃, and at least one of ZrO₂ or HfO₂, and wherein the         glass or glass-ceramic contains not more than 40 percent by         weight collectively SiO₂, B₂O₃, and P₂O₅, based on the total         weight of the glass or glass-ceramic; or     -   i) a glass-ceramic having an average hardness of at least 13         GPa, wherein the glass-ceramic has x, y, and z dimensions each         perpendicular to each other, and wherein each of the x, y, and z         dimensions is at least 5 mm.

In another embodiment, the invention provides a dental material comprising a mixture of a hardenable resin and a ceramic comprising at least one of a glass or glass-ceramic comprising:

-   -   a) at least 35 percent by weight Al₂O₃, based on the total         weight of the glass or glass-ceramic, and a first metal oxide         other than Al₂O₃, wherein the glass or glass-ceramic contains         not more than 10 percent by weight collectively B₂O₃, GeO₂,         P₂O₅, SiO₂, TeO₂, and V₂O₅, based on the total weight of the         glass or glass-ceramic;     -   b) at least 35 percent by weight Al₂O₃, based on the total         weight of the glass or glass-ceramic, and a first metal oxide         other than Al₂O₃, wherein the Al₂O₃ and the first metal oxide         collectively comprise at least 70 percent by weight of the glass         or glass-ceramic;     -   c) Al₂O₃ and at least one of REO or Y₂O₃, wherein at least 80         percent by weight of the glass or glass-ceramic collectively         comprises the Al₂O₃ and the at least one of REO or Y₂O₃, based         on the total weight of the glass or glass-ceramic;     -   d) Al₂O₃, at least one of REO or Y₂O₃, and at least one of ZrO₂         or HfO₂, wherein at least 80 percent by weight of the glass or         glass-ceramic collectively comprises the Al₂O₃, at least one of         REO or Y₂O₃, and at least one of ZrO₂ or HfO₂, based on the         total weight of the glass or glass-ceramic;     -   e) Al₂O₃ and at least one of REO or Y₂O₃, wherein at least 60         percent by weight of the glass or glass-ceramic collectively         comprises the Al₂O₃ and the at least one of REO or Y₂O₃, and         wherein the glass or glass-ceramic contains not more than 20         percent by weight SiO₂ and not more than 20 percent by weight         B₂O₃, based on the total weight of the glass or glass-ceramic;     -   f) Al₂O₃, at least one of REO or Y₂O₃, and at least one of ZrO₂         or HfO₂, wherein at least 60 percent by weight of the glass or         glass-ceramic collectively comprises the Al₂O₃, at least one of         REO or Y₂O₃, and at least one of ZrO₂ or HfO₂, and wherein the         glass or glass-ceramic contains not more than 20 percent by         weight SiO₂ and not more than 20 percent by weight B₂O₃, based         on the total weight of the glass or glass-ceramic;     -   g) Al₂O₃ and at least one of REO or Y₂O₃, wherein at least 60         percent by weight of the glass or glass-ceramic comprise the         Al₂O₃ and the at least one of REO or Y₂O₃, and wherein the glass         or glass-ceramic contains not more than 40 percent by weight         collectively SiO₂, B₂O₃, and P₂O₅, based on the total weight of         the glass or glass-ceramic;     -   h) Al₂O₃, at least one of REO or Y₂O₃, and at least one of ZrO₂         or HfO₂, wherein at least 60 percent by weight of the glass or         glass-ceramic collectively comprises the Al₂O₃, at least one of         REO or Y₂O₃, and at least one of ZrO₂ or HfO₂, and wherein the         glass or glass-ceramic contains not more than 40 percent by         weight collectively SiO₂, B₂O₃, and P₂O₅, based on the total         weight of the glass or glass-ceramic; or     -   i) a glass-ceramic having an average hardness of at least 13         GPa.

In another embodiment, the invention provides a method of making a dental article or an orthodontic appliance comprising the steps of:

-   -   providing a dental or orthodontic mill blank;     -   carving a dental or orthodontic mill blank, wherein the mill         blank comprises a glass or glass-ceramic comprising at least one         of:     -   a) at least 35 percent by weight Al₂O₃, based on the total         weight of the glass or glass-ceramic, and a first metal oxide         other than Al₂O₃, wherein the glass or glass-ceramic contains         not more than 10 percent by weight collectively B₂O₃, GeO₂,         P₂O₅, SiO₂, TeO₂, and V₂O₅, based on the total weight of the         glass or glass-ceramic;     -   b) at least 35 percent by weight Al₂O₃, based on the total         weight of the glass or glass-ceramic, and a first metal oxide         other than Al₂O₃ wherein the Al₂O₃ and the first metal oxide         collectively comprise at least 70 percent by weight of the glass         or glass-ceramic;     -   c) Al₂O₃ and at least one of REO or Y₂O₃, wherein at least 80         percent by weight of the glass or glass-ceramic collectively         comprises the Al₂O₃ and the at least one of REO or Y₂O₃, based         on the total weight of the glass or glass-ceramic;     -   d) Al₂O₃, at least one of REO or Y₂O₃, and at least one of ZrO₂         or HfO₂, wherein at least 80 percent by weight of the glass or         glass-ceramic collectively comprises the Al₂O₃, at least one of         REO or Y₂O₃, and at least one of ZrO₂ or HfO₂, based on the         total weight of the glass or glass-ceramic;     -   e) Al₂O₃ and at least one of REO or Y₂O₃, wherein at least 60         percent by weight of the glass or glass-ceramic collectively         comprises the Al₂O₃ and the at least one of REO or Y₂O₃, and         wherein the glass or glass-ceramic contains not more than 20         percent by weight SiO₂ and not more than 20 percent by weight         B₂O₃, based on the total weight of the glass or glass-ceramic;     -   f) Al₂O₃, at least one of REO or Y₂O₃, and at least one of ZrO₂         or HfO₂, wherein at least 60 percent by weight of the glass or         glass-ceramic collectively comprises the Al₂O₃, at least one of         REO or Y₂O₃, and at least one of ZrO₂ or HfO₂, and wherein the         glass or glass-ceramic contains not more than 20 percent by         weight SiO₂ and not more than 20 percent by weight B₂O₃, based         on the total weight of the glass or glass-ceramic;     -   g) Al₂O₃ and at least one of REO or Y₂O₃, wherein at least 60         percent by weight of the glass or glass-ceramic comprise the         Al₂O₃ and the at least one of REO or Y₂O₃, and wherein the glass         or glass-ceramic contains not more than 40 percent by weight         collectively SiO₂, B₂O₃, and P₂O₅, based on the total weight of         the glass or glass-ceramic;     -   h) Al₂O₃, at least one of REO or Y₂O₃, and at least one of ZrO₂         or HfO₂, wherein at least 60 percent by weight of the glass or         glass-ceramic collectively comprises the Al₂O₃, at least one of         REO or Y₂O₃, and at least one of ZrO₂ or HfO₂, and wherein the         glass or glass-ceramic contains not more than 40 percent by         weight collectively SiO₂, B₂O₃, and P₂O₅, based on the total         weight of the glass or glass-ceramic; or     -   i) a glass-ceramic having an average hardness of at least 13         GPa.

In another embodiment, the invention provides a method of making a dental article or an orthodontic appliance comprising the steps of:

-   -   heating glass above the T_(g) of the glass such that the glass         coalesces or flows to form a dental article or an orthodontic         appliance having a shape; and     -   cooling the coalesced article, wherein the glass comprises at         least one of:     -   a) at least 35 percent by weight Al₂O₃, based on the total         weight of the glass, and a first metal oxide other than Al₂O₃,         wherein the ceramic contains not more than 10 percent by weight         collectively B₂O₃, GeO₂, P₂O₅, SiO₂, TeO₂, and V₂O₅, based on         the total weight of the glass;     -   b) at least 35 percent by weight Al₂O₃, based on the total         weight of the glass, a first metal oxide other than Al₂O₃,         wherein the Al₂O₃ and the first metal oxide collectively         comprise at least 70 percent by weight of the glass;     -   c) Al₂O₃ and at least one of REO or Y₂O₃, wherein at least 80         percent by weight of the glass collectively comprises the Al₂O₃         and the at least one of REO or Y₂O₃, based on the total weight         of the glass;     -   d) Al₂O₃, at least one of REO or Y₂O₃, and at least one of ZrO₂         or HfO₂, wherein at least 80 percent by weight of the glass         collectively comprises the Al₂O₃, at least one of REO or Y₂O₃,         and at least one of ZrO₂ or HfO₂, based on the total weight of         the glass;     -   e) Al₂O₃ and at least one of REO or Y₂O₃, wherein at least 60         percent by weight of the glass collectively comprises the Al₂O₃         and the at least one of REO or Y₂O₃, and wherein the glass         contains not more than 20 percent by weight SiO₂ and not more         than 20 percent by weight B₂O₃, based on the total weight of the         glass;     -   f) Al₂O₃, at least one of REO or Y₂O₃, and at least one of ZrO₂         or HfO₂, wherein at least 60 percent by weight of the glass         collectively comprises the Al₂O₃, at least one of REO or Y₂O₃,         and at least one of ZrO₂ or HfO₂, and wherein the glass contains         not more than 20 percent by weight SiO₂ and not more than 20         percent by weight B₂O₃, based on the total weight of the glass;     -   g) Al₂O₃ and at least one of REO or Y₂O₃, wherein at least 60         percent by weight of the glass comprise the Al₂O₃ and the at         least one of REO or Y₂O₃, and wherein the glass contains not         more than 40 percent by weight collectively SiO₂, B₂O₃, and         P₂O₅, based on the total weight of the glass; or     -   h) Al₂O₃, at least one of REO or Y₂O₃, and at least one of ZrO₂         or HfO₂, wherein at least 60 percent by weight of the glass         collectively comprises the Al₂O₃, at least one of REO or Y₂O₃,         and at least one of ZrO₂ or HfO₂, and wherein the glass contains         not more than 40 percent by weight collectively SiO₂, B₂O₃, and         P₂O₅, based on the total weight of the glass.

In another embodiment, the invention provides a method of making a dental article or an orthodontic appliance comprising the steps of:

-   -   combining a glass or glass-ceramic with a hardenable resin to         form a mixture;     -   forming the dental article or the orthodontic appliance into a         shape; hardening said mixture to form the dental article or         orthodontic appliance, wherein said glass or glass-ceramic         comprises at least one of:     -   a) at least 35 percent by weight Al₂O₃, based on the total         weight of the glass or glass-ceramic, and a first metal oxide         other than Al₂O₃, wherein the glass or glass-ceramic contains         not more than 10 percent by weight collectively B₂O₃, GeO₂,         P₂O₅, SiO₂, TeO₂, and V₂O₅, based on the total weight of the         glass or glass-ceramic;     -   b) at least 35 percent by weight Al₂O₃, based on the total         weight of the glass or glass-ceramic, and a first metal oxide         other than Al₂O₃, wherein the Al₂O₃ and the first metal oxide         collectively comprise at least 70 percent by weight of the glass         or glass-ceramic;     -   c) Al₂O₃ and at least one of REO or Y₂O₃, wherein at least 80         percent by weight of the glass or glass-ceramic collectively         comprises the Al₂O₃ and the at least one of REO or Y₂O₃, based         on the total weight of the glass or glass-ceramic;     -   d) Al₂O₃, at least one of REO or Y₂O₃, and at least one of ZrO₂         or HfO₂, wherein at least 80 percent by weight of the glass or         glass-ceramic collectively comprises the Al₂O₃, at least one of         REO or Y₂O₃, and at least one of ZrO₂ or HfO₂, based on the         total weight of the glass or glass-ceramic;     -   e) Al₂O₃ and at least one of REO or Y₂O₃, wherein at least 60         percent by weight of the glass or glass-ceramic collectively         comprises the Al₂O₃ and the at least one of REO or Y₂O₃, and         wherein the glass or glass-ceramic contains not more than 20         percent by weight SiO₂ and not more than 20 percent by weight         B₂O₃, based on the total weight of the glass or glass-ceramic;     -   f) Al₂O₃, at least one of REO or Y₂O₃, and at least one of ZrO₂         or HfO₂, wherein at least 60 percent by weight of the glass or         glass-ceramic collectively comprises the Al₂O₃, at least one of         REO or Y₂O₃, and at least one of ZrO₂ or HfO₂, and wherein the         glass or glass-ceramic contains not more than 20 percent by         weight SiO₂ and not more than 20 percent by weight B₂O₃, based         on the total weight of the glass or glass-ceramic;     -   g) Al₂O₃ and at least one of REO or Y₂O₃, wherein at least 60         percent by weight of the glass or glass-ceramic comprise the         Al₂O₃ and the at least one of REO or Y₂O₃, and wherein the glass         or glass-ceramic contains not more than 40 percent by weight         collectively SiO₂, B₂O₃, and P₂O₅, based on the total weight of         the glass or glass-ceramic;     -   h) Al₂O₃, at least one of REO or Y₂O₃, and at least one of ZrO₂         or HfO₂, wherein at least 60 percent by weight of the glass or         glass-ceramic collectively comprises the Al₂O₃, at least one of         REO or Y₂O₃, and at least one of ZrO₂ or HfO₂, and wherein the         glass or glass-ceramic contains not more than 40 percent by         weight collectively SiO₂, B₂O₃, and P₂O₅, based on the total         weight of the glass or glass-ceramic; or     -   i) a glass-ceramic having an average hardness of at least 13         GPa.

In another embodiment, the invention provides a method of making a dental article or orthodontic appliance comprising the steps of:

-   -   plasma or thermally spraying particles comprising metal oxide         sources onto a suitable substrate such that the particles         coalesce to form a shaped article; and optionally separating the         shaped article or appliance from the substrate, wherein the         shaped article comprises at least one of:     -   a) at least 35 percent by weight Al₂O₃, based on the total         weight of the glass, and a first metal oxide other than Al₂O₃,         wherein the glass contains not more than 10 percent by weight         collectively B₂O₃, GeO₂, P₂O₅, SiO₂, TeO₂, and V₂O₅, based on         the total weight of the glass;     -   b) at least 35 percent by weight Al₂O₃, based on the total         weight of the glass, and a first metal oxide other than Al₂O₃,         wherein the Al₂O₃ and the first metal oxide collectively         comprise at least 70 percent by weight of the glass;     -   c) Al₂O₃ and at least one of REO or Y₂O₃, wherein at least 80         percent by weight of the glass collectively comprises the Al₂O₃         and the at least one of REO or Y₂O₃, based on the total weight         of the glass;     -   d) Al₂O₃, at least one of REO or Y₂O₃, and at least one of ZrO₂         or HfO₂, wherein at least 80 percent by weight of the glass         collectively comprises the Al₂O₃, at least one of REO or Y₂O₃,         and at least one of ZrO₂ or HfO₂, based on the total weight of         the glass;     -   e) Al₂O₃ and at least one of REO or Y₂O₃, wherein at least 60         percent by weight of the glass collectively comprises the Al₂O₃         and the at least one of REO or Y₂O₃, and wherein the glass         contains not more than 20 percent by weight SiO₂ and not more         than 20 percent by weight B₂O₃, based on the total weight of the         glass;     -   f) Al₂O₃, at least one of REO or Y₂O₃, and at least one of ZrO₂         or HfO₂, wherein at least 60 percent by weight of the glass         collectively comprises the Al₂O₃, at least one of REO or Y₂O₃,         and at least one of ZrO₂ or HfO₂, and wherein the glass contains         not more than 20 percent by weight SiO₂ and not more than 20         percent by weight B₂O₃, based on the total weight of the glass;     -   g) Al₂O₃ and at least one of REO or Y₂O₃, wherein at least 60         percent by weight of the glass comprise the Al₂O₃ and the at         least one of REO or Y₂O₃, and wherein the glass contains not         more than 40 percent by weight collectively SiO₂, B₂O₃, and         P₂O₅, based on the total weight of the glass; or     -   h) Al₂O₃, at least one of REO or Y₂O₃, and at least one of ZrO₂         or HfO₂, wherein at least 60 percent by weight of the glass         collectively comprises the Al₂O₃, at least one of REO or Y₂O₃,         and at least one of ZrO₂ or HfO₂, and wherein the glass contains         not more than 40 percent by weight collectively SiO₂, B₂O₃, and         P₂O₅, based on the total weight of the glass.

In another embodiment, the invention provides a kit comprising a plurality of dental or orthodontic components wherein at least one of the components includes a dental material, dental article, or orthodontic appliance comprising at least one of a glass or glass-ceramic described herein.

In another embodiment, the invention provides a method of performing a dental restoration comprising the steps of: preparing a dental site to be restored; and

-   -   applying a restorative material comprising at least one of a         ceramic, glass, or glass-ceramic described herein.

BRIEF DESCRIPTION OF THE FIGURES

FIG. 1 is a digital image of an optical photomicrograph of a hot-pressed ceramic.

FIG. 2 a is a digital image of a scanning electron microscope (SEM) photomicrograph of a polished section of Example 1 material heat-treated at 1300° C.

FIG. 2 b is a digital image of a scanning electron microscope (SEM) photomicrograph of a polished section of Example 1 material heat-treated at 1400° C.

FIG. 3 is a DTA trace for Example 1 material.

FIG. 4 is a photograph of a dental restoration milled using Example 1 material and a comparative dental restoration milled using standard (PARADIGM MZ100) material.

DETAILED DESCRIPTION

In this application:

-   -   “amorphous material” refers to material derived from a melt         and/or a vapor phase that lacks any long range crystal structure         as determined by x-ray diffraction and/or has an exothermic peak         corresponding to the crystallization of the amorphous material         as determined by a DTA (differential thermal analysis) as         determined by the test described herein entitled “Differential         Thermal Analysis”;     -   “ceramic” includes amorphous material, glass, crystalline         ceramic, glass-ceramic, and combinations thereof;     -   “complex metal oxide” refers to a metal oxide comprising two or         more different metal elements and oxygen (e.g., CeAl₁₀O₁₈,         DY₃Al₅O₁₂, MgA₁₂O₄, and Y₃Al₅O₁₂);     -   “complex Al₂O₃.metal oxide” refers to a complex metal oxide         comprising, on a theoretical oxide basis, Al₂O₃ and one or more         metal elements other than Al (e.g., CeAl₁₁O₁₈, DY₃Al₅O₁₂,         MgA₁₂O₄, and Y₃Al₅O₁₂);     -   “complex Al₂O₃—Y₂O₃” refers to a complex metal oxide comprising,         on a theoretical oxide basis, Al₂O₃ and Y₂O₃ (e.g., Y₃Al₅O₁₂);     -   “complex Al₂O₃.REO” refers to a complex metal oxide comprising,         on a theoretical oxide basis, Al₂O₃ and rare earth oxide (e.g.,         CeAl₁₁O₁₈ and Dy₃Al₅O₁₂);     -   “dental article” refers to a restored dentition or a portion         thereof. Examples include restoratives, replacements, inlays,         onlays, veneers, full and partial crowns, bridges, implants,         implant abutments, copings, anterior fillings, posterior         fillings, cavity liners, sealants, dentures, posts, and bridge         frameworks;     -   “dental material” refers to a dental composition such as a paste         which when hardens forms a dental article;     -   “glass” refers to amorphous material exhibiting a glass         transition temperature;     -   “glass-ceramic” refers to ceramics comprising crystals formed by         heat-treating amorphous material;     -   “hardenable” refers to a material that can be cured or         solidified (e.g., by heating to remove solvent, heating to cause         polymerization, chemical crosslinking, radiation-induced         polymerization or crosslinking, or the like);     -   “hardened” refers to material that is cured or solidified (e.g.,         by heating to remove solvent, heating to cause polymerization,         chemical crosslinking, radiation-induced polymerization or         crosslinking, or the like);     -   “hardening” refers to a method of curing or solidifying (e.g.,         by heating to remove solvent, heating to cause polymerization,         chemical crosslinking, radiation-induced polymerization or         crosslinking, or the like);     -   “orthodontic appliance” refers to any device intended for         mounting on a tooth, and used to transmit to the tooth         corrective force from an arch wire, spring, elastic, or other         force-applying component. Examples include brackets, buccal         tubes, cleats, and buttons;     -   “prosthesis” includes crowns, bridges, inlays, onlays, veneers,         copings, frameworks, and abutments;     -   “restoratives” includes veneers, crowns, inlays, onlays, and         bridge structures;     -   “T_(g)” refers to the glass transition temperature as determined         by the test described herein entitled “Differential Thermal         Analysis”;     -   “T_(x)” refers to the crystallization temperature as determined         by the test described herein entitled “Differential Thermal         Analysis”;     -   “rare earth oxides” refers to cerium oxide (e.g., CeO₂),         dysprosium oxide (e.g., Dy₂O₃), erbium oxide (e.g., Er₂O₃),         europium oxide (e.g., Eu₂O₃), gadolinium (e.g., Gd₂O₃), holmium         oxide (e.g., Ho₂O₃), lanthanum oxide (e.g., La₂O₃), lutetium         oxide (e.g., Lu₂O₃), neodymium oxide (e.g., Nd₂O₃), praseodymium         oxide (e.g., Pr₆O₁₁), samarium oxide (e.g., Sm₂O₃), terbium         (e.g., Tb₂O₃), thorium oxide (e.g., Th₄O₇), thulium (e.g.,         Tm₂O₃), and ytterbium oxide (e.g., Yb₂O₃), and combinations         thereof; and     -   “REO” refers to rare earth oxide(s).

Further, it is understood herein that unless it is stated that a metal oxide (e.g., Al₂O₃, complex Al₂O₃.metal oxide, etc.) is crystalline, for example, in a glass-ceramic, it may be amorphous, crystalline, or portions amorphous, and portions crystalline. For example, if a glass-ceramic comprises Al₂O₃ and ZrO₂, the Al₂O₃ and ZrO₂ may each be in an amorphous state, crystalline state, or portions in an amorphous state and portions in a crystalline state, or even as a reaction product with another metal oxide(s) (e.g., unless it is stated that, for example, Al₂O₃ is present as crystalline Al₂O₃ or a specific crystalline phase of Al₂O₃ (e.g., alpha Al₂O₃), it may be present as crystalline Al₂O₃ and/or as part of one or more crystalline complex Al₂O₃.metal oxides).

Further, it is understood that glass-ceramics formed by heating amorphous material not exhibiting a T_(g) may not actually comprise glass, but rather may comprise the crystals and amorphous material that does not exhibiting a T_(g).

Some advantages of using the ceramics, glasses, and glass-ceramics described herein for dental and orthodontic applications include improved processing abilities of complex-shaped articles combined with excellent material properties that are akin to those of structural ceramics (e.g., Al₂O₃ and ZrO₂). These useful dental shapes can be generated by either glass-like viscous flow or by machining blanks in amorphous or partially crystalline states.

Ceramics, Glass, and Glass-Ceramics

In some embodiments according to the present invention, the ceramic, the glass and the glass-ceramic comprises at least 35 (in some embodiments, at least 40, 45, 50, 55, 60, 65, 70, or even at least 75) percent by weight Al₂O₃, based on the total weight of the ceramic, glass, or glass-ceramic, respectively, and a first metal oxide other than Al₂O₃ (e.g., Y₂O₃, REO, MgO, TiO₂, Cr₂O₃, CuO, NiO, and Fe₂O₃), and optionally a second, (third, etc.) different metal oxide other than Al₂O₃ (e.g., Y₂O₃, REO, MgO, TiO₂, Cr₂O₃, CuO, NiO, and, Fe₂O₃), wherein the glass or glass-ceramic, respectively, contains not more than 10 (in some embodiments, not more than 5, 4, 3, 2, 1, or zero) percent by weight collectively B₂O₃, GeO₂, P₂O₅, SiO₂, TeO₂, and V₂O₅, based on the total weight of the glass or glass-ceramic, respectively. Embodiments of the glass-ceramic have an average hardness of at least 13 GPa, 14 GPa, 15 GPa, 16 GPa, 17 GPa, 18 GPa, or even at least 19 GPa.

In some embodiments according to the present invention, the glass and the glass-ceramic comprises at least 35 (in some embodiments, at least 40, 45, 50, 55, 60, 65, 70, or even at least 75) percent by weight Al₂O₃, based on the total weight of the ceramic, glass, or glass-ceramic, respectively, and a first metal oxide other than Al₂O₃ (e.g., Y₂O₃, REO, MgO, TiO₂, Cr₂O₃, CuO, NiO, and Fe₂O₃), and optionally, a second, (third etc.) different metal oxide other than Al₂O₃ (e.g., Y₂O₃, REO, MgO, TiO₂, Cr₂O₃, CuO, NiO, and, Fe₂O₃), wherein the Al₂O₃, first metal oxide, and second metal oxide collectively comprise at least 80 (in some embodiments, at least 85, 90, 95, or 100) percent by weight of the ceramic, glass, or glass-ceramic, respectively, and wherein the ceramic, glass, or glass-ceramic contains not more than 20 (in some embodiments, not more than 15, 10, 5, 4, 3, 2, 1, or even zero) percent by weight collectively B₂O₃, GeO₂, P₂O₅, SiO₂, TeO₂, and V₂O₅, based on the total weight of the ceramic, glass, or glass-ceramic, respectively. Embodiments of the glass-ceramic have an average hardness of at least 13 GPa, 14 GPa, 15 GPa, 16 GPa, 17 GPa, 18 GPa, or even at least 19 GPa.

In some embodiments according to the present invention, the ceramic, the glass, and the glass-ceramic comprises Al₂O₃ and at least one of REO or Y₂O₃, wherein at least 80 (in some embodiments, at least 85, 90, 95, or even 100) percent by weight of the ceramic, glass, or glass-ceramic, respectively, collectively comprises the Al₂O₃ and the at least one of REO or Y₂O₃, based on the total weight of the ceramic, glass, or glass-ceramic, respectively.

In some embodiments according to the present invention, the ceramic, the glass, and the glass-ceramic comprises Al₂O₃, at least one of REO or Y₂O₃, and at least one of ZrO₂ or HfO₂, wherein at least 80 (in some embodiments, at least 85, 90, 95, or even 100) percent by weight of the ceramic, glass, or glass-ceramic, respectively, collectively comprises the Al₂O₃, at least one of REO or Y₂O₃, and at least one of ZrO₂ or HfO₂, based on the total weight of the ceramic, glass, or glass-ceramic, respectively. Embodiments of the glass-ceramic have an average hardness of at least 13 GPa, 14 GPa, 15 GPa, 16 GPa, 17 GPa, 18 GPa, or even at least 19 GPa.

In some embodiments according to the present invention, the ceramic, the glass, and the glass-ceramic comprises Al₂O₃ and at least one of REO or Y₂O₃, wherein at least 60 (in some embodiments, 65, 70, 75, 80, 85, 90, 95, or even at least 100) percent by weight of the ceramic, glass, or glass-ceramic, respectively, collectively comprises the Al₂O₃ and the at least one of REO or Y₂O₃, and wherein the ceramic, glass, or glass-ceramic, respectively, contains not more than 20 (in some embodiments, not more than 15, 10, 5, or even zero) percent by weight SiO₂ and not more than 20 (in some embodiments, not more than 15, 10, 5, or even zero) percent by weight B₂O₃, based on the total weight of the ceramic, glass, or glass-ceramic, respectively. Embodiments of the glass-ceramic have an average hardness of at least 13 GPa, 14 GPa, 15 GPa, 16 GPa, 17 GPa, 18 GPa, or even at least 19 GPa.

In some embodiments according to the present invention, the ceramic, the glass, and the glass-ceramic comprises Al₂O₃, at least one of REO or Y₂O₃, and at least one of ZrO₂ or HfO₂, wherein at least 60 (in some embodiments, 65, 70, 75, 80, 85, 90, 95, or even at least 100) percent by weight of the ceramic, glass, or glass-ceramic, respectively, collectively comprises the Al₂O₃, at least one of REO or Y₂O₃, and at least one of ZrO₂ or HfO₂, and wherein the ceramic, glass, or glass-ceramic, respectively, contains not more than 20 (in some embodiments, less than 15, 10, 5, or even zero) percent by weight SiO₂ and not more than 20 (in some embodiments, not more than 15, 10, 5, or even zero) percent by weight B₂O₃, based on the total weight of the ceramic, glass, or glass-ceramic, respectively. Embodiments of the glass-ceramic have an average hardness of at least 13 GPa, 14 GPa, 15 GPa, 16 GPa, 17 GPa, 18 GPa, or even at least 19 GPa.

In some embodiments according to the present invention, the ceramic, the glass, and the glass-ceramic comprises Al₂O₃ and at least one of REO or Y₂O₃, wherein at least 60 (in some embodiments, 65, 70, 75, 80, 85, 90, 95, or even at least 100) percent by weight of the ceramic, glass, or glass-ceramic, respectively, comprise the Al₂O₃ and the at least one of REO or Y₂O₃, and wherein the ceramic, glass, or glass-ceramic, respectively, contains not more than 40 (in some embodiments, not more than 35, 30, 25, 20, 15, 10, 5, or even zero) percent by weight collectively SiO₂, B₂O₃, and P₂O₅, based on the total weight of the ceramic, glass, or glass-ceramic, respectively. Embodiments of the glass-ceramic have an average hardness of at least 13 GPa, 14 GPa, 15 GPa, 16 GPa, 17 GPa, 18 GPa, or even at least 19 GPa.

In some embodiments according to the present invention, the ceramic, the glass, and the glass-ceramic comprises Al₂O₃, at least one of REO or Y₂O₃, and at least one of ZrO₂ or HfO₂, wherein at least 60 (in some embodiments, 65, 70, 75, 80, 85, 90, 95, or even at least 100) percent by weight of the ceramic, glass, or glass-ceramic, respectively, collectively comprises the Al₂O₃, at least one of REO or Y₂O₃, and at least one of ZrO₂ or HfO₂, and wherein the ceramic, glass, or glass-ceramic, respectively, contains not more than 40 (in some embodiments, not more than 35, 30, 25, 20, 15, 10, 5, or even zero) percent by weight collectively SiO₂, B₂O₃, and P₂O₅, based on the total weight of the ceramic, glass, or glass-ceramic, respectively. Embodiments of the glass-ceramic have an average hardness of at least 13 GPa, 14 GPa, 15 GPa, 16 GPa, 17 GPa, 18 GPa, or even at least 19 GPa.

Some embodiments of glass-ceramics according to the present invention may comprise, for example, at least 1, 2, 3, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, or even 100 percent by volume glass. Some embodiments of glass-ceramics according to the present invention may comprise, for example, at least 1, 2, 3, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, 97, 98, 99, or even 100 percent by volume crystalline ceramic, based on the total volume of the glass-ceramic.

Some amorphous materials used to make glasses and the glass-ceramics made therefrom, comprise 20 to at least 70 percent by weight (in some embodiments, 30 to at least 70 percent, 40 to at least 70 percent, 50 to at least 70 percent, or even 60 to at least 70 percent) Al₂O₃; 0 to 70 percent by weight (in some embodiments, 0 to 25 percent, or even 0 to 10 percent) Y₂O₃; and 0 to 70 percent by weight (in some embodiments, 0 to 50 percent, 0 to 25 percent, or even 0 to 10 percent) at least one of ZrO₂ or HfO₂, based on the total weight of the amorphous material or glass-ceramic. In some embodiments, such amorphous materials, and the glass-ceramics made therefrom, comprise at least 30 percent by weight, at least 40 percent by weight, at least 50 percent by weight, at least 60 percent by weight, or even at least 70 percent by weight Al₂O₃, based on the total weight of the amorphous material or glass-ceramic. In some embodiments, such amorphous materials, and the glass-ceramics made therefrom, contain less than 40 (in some embodiments, less than 35, 30, 25, 20, 15, 10, 5, 4, 3, 2, 1, or even zero) percent by weight collectively SiO₂, B₂O₃, and P₂O₅, based on the total weight of the amorphous material or glass-ceramic. In some embodiments, such amorphous materials, and the glass-ceramics made therefrom, contain less than 20 (in some embodiments, less than 15, 10, 5, or even zero) percent by weight SiO₂ and less than 20 (preferably, less than 15, 10, 5, or even zero) percent by weight B₂O₃, based on the total weight of the amorphous material or glass-ceramic.

Some amorphous materials used to make glasses and the glass-ceramics made therefrom, comprise 20 to at least 70 percent by weight (in some embodiments, 30 to at least 70 percent, 40 to at least 70 percent, 50 to at least 70 percent, or even 60 to at least 70 percent) Al₂O₃; 0 to 70 percent by weight (in some embodiments, 0 to 50 percent, 0 to 25 percent, or even 0 to 10 percent) REO; 0 to 50 percent by weight (in some embodiments, 0 to 25 percent, or even 0 to 10 percent) at least one of ZrO₂ or HfO₂, based on the total weight of the amorphous material or glass-ceramic. In some embodiments, such amorphous materials, and the glass-ceramics made therefrom, comprise 30 percent by weight, at least 40 percent by weight, at least 50 percent by weight, at least 60 percent by weight, or even at least 70 percent by weight Al₂O₃, based on the total weight of the amorphous material or glass-ceramic. In some embodiments, such amorphous materials, and the glass-ceramics made therefrom, comprise less than 40 (in some embodiments, less than 35, 30, 25, 20, 15, 10, 5, 4, 3, 2, 1, or even zero) percent by weight collectively SiO₂, B₂O₃, and P₂O₅, based on the total weight of the amorphous materials or glass-ceramic. In some embodiments, such glasses, and the glass-ceramics made therefrom, contain less than 20 (in some embodiments, less than 15, 10, 5, or even zero) percent by weight SiO₂ and less than 20 (in some embodiments, less than 15, 10, 5, or even zero) percent by weight B₂O₃, based on the total weight of the amorphous material or glass-ceramic.

Some amorphous materials used to make glasses and the glass-ceramics made therefrom, comprise 20 to at least 70 percent by weight (in some embodiments, 30 to at least 70 percent, 40 to at least 70 percent, 50 to at least 70 percent, or even 60 to 70 percent) Al₂O₃; 0 to 70 percent by weight (in some embodiments, 0 to 50 percent, 0 to 25 percent, or even 0 to 10 percent) Y₂O₃; 0 to 70 percent by weight (in some embodiments, 0 to 50 percent, 0 to 25 percent, or even 0 to 10 percent) REO; 0 to 50 percent by weight (in some embodiments, 0 to 25 percent, or even 0 to 10 percent) at least one of ZrO₂ or HfO₂, based on the total weight of the amorphous material or glass-ceramic. In some embodiments, such amorphous materials, and the glass-ceramics made therefrom, comprise at least 30 percent by weight, at least 40 percent by weight, at least 50 percent by weight, at least 60 percent by weight, or even at least 70 percent by weight Al₂O₃, based on the total weight of the amorphous material or glass-ceramic. In some embodiments, such amorphous materials, and the glass-ceramics made therefrom, contain less than 40 (in some embodiments, less than 35, 30, 25, 20, 15, 10, 5, 4, 3, 2, 1, or even zero) percent by weight collectively SiO₂, B₂O₃, and P₂O₅, based on the total weight of the amorphous material or glass-ceramic. In some embodiments, such amorphous materials, and the glass-ceramics made therefrom, contain less than 20 (in some embodiments, less than 15, 10, 5, or even zero) percent by weight SiO₂ and less than 20 (in some embodiments, less than 15, 10, 5, or even zero) percent by weight B₂O₃, based on the total weight of the amorphous material or glass-ceramic.

Amorphous materials (e.g., glasses), ceramics comprising the amorphous material, particles comprising the amorphous material, etc. can be made, for example, by heating (including in a flame) the appropriate metal oxide sources to form a melt, desirably a homogenous melt, and then rapidly cooling the melt to provide amorphous material. The metal oxide sources and other additives can be in any form suitable to the process and equipment used to make the glass or glass-ceramics. Desirable cooling rates include those of 10K/s and greater. Embodiments of amorphous materials can be made, for example, by melting the metal oxide sources in any suitable furnace (e.g., an inductive heated furnace, a gas-fired furnace, or an electrical furnace), or, for example, in a plasma. The resulting melt is cooled (e.g., discharging the melt into a cooling media (e.g., high velocity air jets, liquids, metal plates (including chilled metal plates), metal rolls (including chilled metal rolls), metal balls (including chilled metal balls), and the like)).

Further, other techniques for making melts and glasses, and otherwise forming amorphous material include vapor phase quenching, melt-extraction, plasma spraying, and gas or centrifugal atomization. For additional details regarding plasma spraying, see, for example, U.S. Publication No. 2004-0023078 A1, the disclosure of which is incorporated herein by reference.

Gas atomization involves melting feed particles to convert them to melt. A thin stream of such melt is atomized through contact with a disruptive air jet (i.e., the stream is divided into fine droplets). The resulting substantially discrete, generally ellipsoidal amorphous material comprising particles (e.g., beads) are then recovered. Examples of bead sizes include those having a diameter in a range of about 5 micrometers to about 3 mm. Melt-extraction can be carried out, for example, as disclosed in U.S. Pat. No. 5,605,870, the disclosure of which is incorporated herein by reference. Containerless glass forming techniques utilizing laser beam heating as disclosed, for example, in U.S. Pat. No. 6,482,758, the disclosure of which is incorporated herein by reference, may also be useful in making glass, glass-ceramics and amorphous materials.

Embodiments of amorphous material can be made utilizing flame fusion as disclosed, for example, in U.S. Pat. No. 6,254,981, the disclosure of which is incorporated herein by reference. In this method, the metal oxide sources materials are fed (e.g., in the form of particles, sometimes referred to as “feed particles”) directly into a burner (e.g., a methane-air burner, an acetylene-oxygen burner, a hydrogen-oxygen burner, and like), and then quenched, for example, in water, cooling oil, air, or the like. Feed particles can be formed, for example, by grinding, agglomerating (e.g., spray-drying), melting, or sintering the metal oxide sources. The size of feed particles fed into the flame generally determine the size of the resulting amorphous material comprising particles.

Embodiments of amorphous materials can also be obtained by other techniques, such as: laser spin melt with free fall cooling, Taylor wire technique, plasmatron technique, hammer and anvil technique, centrifugal quenching, air gun splat cooling, single roller and twin roller quenching, roller-plate quenching and pendant drop melt extraction (see, e.g., Rapid Solidification of Ceramics, Brockway et. al, Metals And Ceramics Information Center, A Department of Defense Information Analysis Center, Columbus, Ohio, January, 1984, the disclosure of which is incorporated here as a reference). Embodiments of amorphous materials may also be obtained by other techniques, such as: thermal (including flame or laser or plasma-assisted) pyrolysis of suitable precursors, physical vapor synthesis (PVS) of metal precursors and mechanochemical processing.

The cooling rate is believed to affect the properties of the quenched amorphous material. For instance, glass transition temperature, density, and other properties of glass typically change with cooling rates.

Rapid cooling may also be conducted under controlled atmospheres, such as a reducing, neutral, or oxidizing environment to maintain and/or influence the desired oxidation states, etc. during cooling. The atmosphere can also influence amorphous material formation by influencing crystallization kinetics from undercooled liquid. For example, larger undercooling of Al₂O₃ melts without crystallization has been reported in argon atmosphere as compared to that in air.

Amorphous materials can also be made by a sol-gel process. The sol-gel process comprises the steps of forming a precursor composition in the form of a dispersion, sol, or solution in an aqueous or organic liquid medium. The precursor composition can be processed into a variety of useful forms including coatings, films, powders, gels, aerogels, dense bulk shapes, fibers, flakes, granules, and nanoclusters. Further details of these processes can be found in Sol-Gel Science by C. Jeffrey Brinker and George W. Scherer (Academic Press, 1990), the disclosure of which is incorporated herein by reference. Further details about the synthesis of nanoclusters can be found in PCT Publication No. WO 0130306(A1), the disclosure of which is incorporated herein by reference. Another method of making powders is by the spray pyrolysis of a precursor containing one or more glycolato polymetallooxanes dissolved in a volatile organic solvent; details about this process can be found in U.S. Pat. No. 5,958,361, the disclosure of which is incorporated herein by reference.

Useful amorphous material formulations include those at or near a eutectic composition(s) (e.g., binary and ternary eutectic compositions). In addition to compositions disclosed herein, other compositions, including quaternary and other higher order eutectic compositions, may be apparent to those skilled in the art after reviewing the present disclosure.

Sources, including commercial sources, of (on a theoretical oxide basis) Al₂O₃ include bauxite (including both natural occurring bauxite and synthetically produced bauxite), calcined bauxite, hydrated aluminas (e.g., boehmite and gibbsite), aluminum, Bayer process alumina, aluminum ore, gamma alumina, alpha alumina, aluminum salts, aluminum nitrates, and combinations thereof. The Al₂O₃ source may contain, or only provide, Al₂O₃. Alternatively, the Al₂O₃ source may contain, or provide Al₂O₃, as well as one or more metal oxides other than Al₂O₃ (including materials of or containing complex Al₂O₃.metal oxides (e.g., Dy₃Al₅O₁₂, Y₃Al₅O₁₂, CeAl₁₁O₁₈, etc.)).

Sources, including commercial sources, of rare earth oxides include rare earth oxide powders, rare earth metals, rare earth-containing ores (e.g., bastnasite and monazite), rare earth salts, rare earth nitrates, and rare earth carbonates. The rare earth oxide(s) source may contain, or only provide, rare earth oxide(s). Alternatively, the rare earth oxide(s) source may contain, or provide rare earth oxide(s), as well as one or more metal oxides other than rare earth oxide(s) (including materials of or containing complex rare earth oxides.or other metal oxides (e.g., DY₃Al₅O₁₂, CeAl₁₁O₁₈, etc.)).

Sources, including commercial sources, of (on a theoretical oxide basis) Y₂O₃ include yttrium oxide powders, yttrium, yttrium-containing ores, and yttrium salts (e.g., yttrium carbonates, nitrates, chlorides, hydroxides, and combinations thereof). The Y₂O₃ source may contain, or only provide, Y₂O₃. Alternatively, the Y₂O₃ source may contain, or provide Y₂O₃, as well as one or more metal oxides other than Y₂O₃ (including materials of or containing complex Y₂O₃.metal oxides (e.g., Y₃Al₅O₁₂)).

Sources, including commercial sources, of (on a theoretical oxide basis) ZrO₂ include zirconium oxide powders, zircon sand, zirconium, zirconium-containing ores, and zirconium salts (e.g., zirconium carbonates, acetates, nitrates, chlorides, hydroxides, and combinations thereof). In addition, or alternatively, the ZrO₂ source may contain, or provide ZrO₂, as well as other metal oxides such as hafnia. Sources, including commercial sources, of (on a theoretical oxide basis) HfO₂ include hafnium oxide powders, hafnium, hafnium-containing ores, and hafnium salts. In addition, or alternatively, the HfO₂ source may contain, or provide HfO₂, as well as other metal oxides such as ZrO₂.

Other useful metal oxide may also include, on a theoretical oxide basis, BaO, CaO, Cr₂O₃, CoO, Fe₂O₃, GeO₂, Li₂O, MgO, MnO, NiO, Na₂O, Sc₂O₃, SrO, TiO₂, ZnO, and combinations thereof. Sources, including commercial sources, include the oxides themselves, complex oxides, ores, carbonates, acetates, nitrates, chlorides, hydroxides, etc. These metal oxides are added to modify a physical property of the resulting particles and/or improve processing. These metal oxides are typically added anywhere from 0 to 50 percent by weight, in some embodiments preferably 0 to 25 percent by weight and more preferably 0 to 50 percent by weight of the glass-ceramic depending, for example, upon the desired property.

The particular selection of metal oxide sources and other additives for making ceramics typically takes into account, for example, the desired composition and microstructure of the resulting ceramics, the desired degree of crystallinity, if any, the desired physical properties (e.g., hardness or toughness) of the resulting ceramics, avoiding or minimizing the presence of undesirable impurities, the desired characteristics of the resulting ceramics, and/or the particular process (including equipment and any purification of the raw materials before and/or during fusion and/or solidification) being used to prepare the ceramics.

In some instances, it may be preferred to incorporate limited amounts of metal oxides selected from the group consisting of: Na₂O, P₂O₅, SiO₂, TeO₂, V₂O₅, and combinations thereof. Sources, including commercial sources, include the oxides themselves, complex oxides, ores, carbonates, acetates, nitrates, chlorides, hydroxides, etc. These metal oxides may be added, for example, to modify a physical property of the resulting particles and/or improve processing. These metal oxides when used are typically added from greater than 0 to 20 percent by weight, preferably greater than 0 to 5 percent by weight and more preferably greater than 0 to 2 percent by weight of the glass-ceramic depending, for example, upon the desired property.

The addition of certain metal oxides may alter the properties and/or crystalline structure or microstructure of a glass-ceramic, as well as the processing of the raw materials and intermediates in making the glass-ceramic. For example, oxide additions such as MgO, CaO, Li₂O, and Na₂O have been observed to alter both the T_(g) (for a glass) and T_(x) (wherein T_(x) is the crystallization temperature) of amorphous material. Although not wishing to be bound by theory, it is believed that such additions influence glass formation. Further, for example, such oxide additions may decrease the melting temperature of the overall system (i.e., drive the system toward lower melting eutectic), and ease of amorphous material-formation. Complex eutectics in multi-component systems (quaternary, etc.) may result in better amorphous material-forming ability. The viscosity of the liquid melt and viscosity of the glass in its “working” range may also be affected by the addition of certain metal oxides such as MgO, CaO, Li₂O, and Na₂O. It is also within the scope of the present invention to incorporate at least one of halogens (e.g., fluorine and chlorine), or chalcogenides (e.g., sulfides, selenides, and tellurides) into the amorphous materials, and the glass-ceramics made therefrom.

Crystallization of the amorphous material and ceramic comprising the amorphous material may also be affected by the additions of certain materials. For example, certain metals, metal oxides (e.g., titanates and zirconates), and fluorides, for example, may act as nucleation agents resulting in beneficial heterogeneous nucleation of crystals. Also, addition of some oxides may change nature of metastable phases devitrifying from the amorphous material upon reheating. In another aspect, for ceramics comprising crystalline ZrO₂, it may be desirable to add metal oxides (e.g., Y₂O₃, TiO₂, CaO, and MgO) that are known to stabilize tetragonal/cubic form of ZrO₂.

The microstructure or phase composition (glassy/amorphous/crystalline) of a material can be determined in a number of ways. Various information can be obtained using optical microscopy, electron microscopy, differential thermal analysis (DTA), and x-ray diffraction (XRD), for example.

Using optical microscopy, amorphous material is typically predominantly transparent due to the lack of light scattering centers such as crystal boundaries, while crystalline material shows a crystalline structure and is opaque due to light scattering effects.

Using DTA, the material is classified as amorphous if the corresponding DTA trace of the material contains an exothermic crystallization event (T_(x)). If the same trace also contains an endothermic event (T_(g)) at a temperature lower than T_(x), it is considered to consist of a glass phase. If the DTA trace of the material contains no such events, it is considered to contain crystalline phases.

Differential thermal analysis (DTA) can be conducted using the following method. DTA runs can be made (using an instrument such as that obtained from Netzsch Instruments, Seib, Germany, under the trade designation “NETZSCH STA 409 DTA/TGA”) using a −140+170 mesh size fraction (i.e., the fraction collected between 105-micrometer opening size and 90-micrometer opening size screens). An amount of each screened sample (typically about 400 milligrams (mg)) is placed in a 100-microliter Al₂O₃ sample holder. Each sample is heated in static air at a rate of 10° C./minute from room temperature (about 25° C.) to 1100° C.

Using powder x-ray diffraction, XRD, (using an x-ray diffractometer such as that obtained under the trade designation “PHILLIPS XRG 3100” from Phillips, Mahwah, N.J., with copper K_(α1) radiation of 1.54050 Angstrom) the phases present in a material can be determined by comparing the peaks present in the XRD trace of the crystallized material to XRD patterns of crystalline phases provided in JCPDS (Joint Committee on Powder Diffraction Standards) databases, published by International Center for Diffraction Data. Furthermore, an XRD can be used qualitatively to determine types of phases. The presence of a broad diffused intensity peak is taken as an indication of the amorphous nature of a material. The existence of both a broad peak and well-defined peaks is taken as an indication of existence of crystalline matter within an amorphous matrix.

The initially formed amorphous material or ceramic (including glass prior to crystallization) may be larger in size than that desired. The amorphous material or ceramic can be converted into smaller pieces using crushing and/or comminuting techniques known in the art, including roll crushing, canary milling, jaw crushing, hammer milling, ball milling, jet milling, impact crushing, and the like. The shape of the ceramic (including glass prior to crystallization) may depend, for example, on the composition and/or microstructure of the ceramic, the geometry in which it was cooled, and the manner in which the ceramic is crushed (i.e., the crushing technique used). In general, where a “blocky” shape is preferred, more energy may be employed to achieve this shape. Conversely, where a “sharp” shape is preferred, less energy may be employed to achieve this shape. The crushing technique may also be changed to achieve different desired shapes. The resulting particles may have an average aspect ratio ranging from 1:1 to 5:1, typically 1.25:1 to 3:1, and preferably 1.5:1 to 2.5:1.

It is also within the scope of the present invention, for example, to directly form ceramic (including glass prior to crystallization) in desired shapes. For example, ceramic (including glass prior to crystallization) may be formed (including molded) by pouring or forming the melt into a mold.

It is also within the scope of the present invention, for example, to fabricate the ceramic (including glass prior to crystallization) by coalescing. This coalescing step in essence forms a larger sized body from two or more smaller particles. For example, amorphous material comprising particles (obtained, for example, by crushing) (including beads and microspheres), fibers, etc. may be formed into an article. For example, ceramic (including glass prior to crystallization), may also be provided by heating, for example, particles comprising the amorphous material, and/or fibers, etc. above the T_(g) such that the particles, etc. coalesce to form a shape and cooling the coalesced shape. The temperature and pressure used for coalescing may depend, for example, upon composition of the amorphous material and the desired density of the resulting material. The temperature should be desirably below glass crystallization temperature, and for glasses, greater than the glass transition temperature. In some embodiments, the temperature used in coalescing may exceed the glass crystallization temperature. In certain embodiments, the heating is conducted at a temperature in a range of about 850° C. to about 1100° C. (in some embodiments, preferably 900° C. to 1000° C.). Typically, the amorphous material is under pressure (e.g., greater than zero to 1 GPa or more) during coalescence to aid the coalescence of the amorphous material.

In one embodiment, a charge of the particles, etc. is placed into a die and hot-pressing is performed at temperatures above glass transition where viscous flow of glass leads to coalescence into a relatively large part. Examples of typical coalescing techniques include hot pressing, hot isostatic pressure, hot extrusion, and the like. During this coalescence step, articles of complex shapes can be obtained by choosing suitable die constructions. Typically, it is generally preferred to cool the resulting coalesced body before further heat treatment.

In another embodiment, a coalesced perform comprising glass is placed into a die and is molded into useful shapes under the action of heat and pressure such that the perform flows. The perform may be glassy or partially crystalline. The perform may have a range of densities of from 50 to 100 of theoretical densities.

It is also within the scope of the present invention to conduct additional heat-treatment to further improve desirable properties of the material. For example, hot-isostatic pressing may be conducted (e.g., at temperatures from about 900° C. to about 1400° C.) to remove residual porosity, increasing the density of the material. Optionally, the resulting, coalesced article can be heat-treated to provide glass-ceramic, crystalline ceramic, or ceramic otherwise comprising crystalline ceramic.

Coalescence of the amorphous material and/or glass-ceramic (e.g., particles) may also be accomplished by a variety of methods, including pressureless or pressure sintering (e.g., sintering, plasma assisted sintering, hot pressing, HIPing, hot forging, hot extrusion, etc.). Coalescence of the amorphous material and/or glass-ceramic or shaping of an already coalesced body may be accomplished with the use of suitable dental presses that can deliver the required temperature and heat. One embodiment of this process comprises the steps of forming a refractory investment mold, inserting the material into the mold, heating, applying pressure to the material such that it fills the mold cavity to form the desired shape. An example of such a process is described in U.S. Pat. No. 6,465,106, incorporated by reference herein. A commercial example of such a press is the Intra-Tech ProPress 100 (Whip-Mix Inc., Farmington, Ky.).

In another embodiment, the materials of this invention can be formed into mill blanks and machined to a desired shaped product. The machining step can be accomplished in glassy, crystalline, or intermediate stages. Digitized CAD/CAM machining can be employed for this task. Examples of such systems include CEREC (Sirona Dental Systems GmbH, Bensheim, Germany) and Lava (3M Company, St. Paul, Minn.). It has been surprisingly found that despite the high-strength nature of the material, it is quite machinable.

Heat-treatment can be carried out in any of a variety of ways, including those known in the art for heat-treating glass to provide glass-ceramics. For example, heat-treatment can be conducted in batches, for example, using resistive, inductively, or gas heated furnaces. Alternatively, for example, heat-treatment can be conducted continuously, for example, using a rotary kiln, fluidized bed furnace, or pendulum kiln. In the case of a rotary kiln or pendulum kiln, the material is fed directly into a kiln operating at the elevated temperature. The time at the elevated temperature may range from a few seconds (in some embodiments even less than 5 seconds) to a few minutes to several hours. The temperature may range anywhere from the T_(x) of the amorphous material to 1600° C., from 900° C. to 1600° C., or between 1200° C. to 1500° C.

The glass is heat-treated to at least partially crystallize the amorphous material to provide glass-ceramic. The heat-treatment of certain glasses to form glass-ceramics is well known in the art. The heating conditions are generally carefully controlled to nucleate and grow crystals to provide desired microstructure and properties. One skilled in the art can determine the appropriate conditions from a Time-Temperature-Transformation (TTT) study of the glass using techniques known in the art. One skilled in the art, after reading the disclosure of the present invention should be able to provide TIT curves for glasses, determine the appropriate nucleation and/or crystal growth conditions to provide glass-ceramics.

In some embodiments of the present invention, the glasses or ceramics comprising glass may be annealed prior to heat-treatment. In such cases, annealing is typically done at a temperature less than the T_(x) of the glass for a time from a few seconds to a few hours or even days. Typically, the annealing is done for a period of less than 3 hours, or even less than an hour. Optionally, annealing may also be carried out in atmospheres other than air.

Heat-treatment may occur, for example, by feeding the material directly into a furnace at the elevated temperature. Alternatively, for example, the material may be fed into a furnace at a much lower temperature (e.g., room temperature) and then heated to desired temperature at a predetermined heating rate. It is within the scope of the present invention to conduct heat-treatment in an atmosphere other than air. In some cases it might be even desirable to heat-treat in a reducing atmosphere(s). Also, for example, it may be desirable to heat-treat under gas pressure as in, for example, hot-isostatic press, or in gas pressure furnace. Although not wanting to be bound by theory, it is believed that the T_(g) and T_(x), as well as the T_(x)-T_(g) of glasses according to the present application may shift depending upon the atmospheres used during the heat treatment. It is also believed that the choice of atmospheres may affect oxidation states of some of the components of the glasses and glass-ceramics. Such variation in oxidation state can bring about varying coloration of glasses and glass-ceramics. In addition, nucleation and crystallization steps can be affected by atmospheres (e.g., the atmosphere may affect the atomic mobilities of some species of the glasses).

Typically, glass-ceramics are stronger than the amorphous materials from which they are formed. Hence, the strength of the material may be adjusted, for example, by the degree to which the amorphous material is converted to crystalline ceramic phase(s). Alternatively, or in addition, the strength of the material may also be affected, for example, by the number of nucleation sites created, which may in turn be used to affect the number, and in turn the size of the crystals of the crystalline phase(s). For additional details regarding forming glass-ceramics, see, for example Glass-Ceramics, P. W. McMillan, Academic Press, Inc., 2nd edition, 1979, the disclosure of which is incorporated herein by reference.

As compared to many other types of ceramic processing (e.g., sintering of a calcined material to a dense, sintered ceramic material), there is relatively little shrinkage (typically, less than 30 percent by volume; in some embodiments, less than 20 percent, 10 percent, 5 percent, or even less than 3 percent by volume) during crystallization of the glass to form the glass-ceramic. The actual amount of shrinkage depends, for example, on the composition of the glass, the heat-treatment time, the heat-treatment temperature, the heat-treatment pressure, the density of the glass being crystallized, the relative amount(s) of the crystalline phases formed, and the degree of crystallization. The amount of shrinkage can be measured by conventional techniques known in the art, including by dilatometry, Archimedes method, or measuring the dimensions material before and after heat-treatment. In cases, there may be some evolution of volatile species during heat-treatment.

For example, during heat-treatment of some exemplary amorphous materials containing ZrO₂ for making glass-ceramics according to present invention, formation of phases such as La₂Zr₂O₇, (Zr, M)O₂ solid solution with face-centered cubic structure (where M=stabilizing cation), cubic/tetragonal ZrO₂, in some cases monoclinic ZrO₂, have been observed at temperatures above about 900° C. Although not wanting to be bound by theory, it is believed that zirconia-related phases are the first phases to nucleate from the amorphous material. In amorphous materials that do not contain ZrO₂ formation of Al₂O₃, ReAlO₃ (wherein Re is at least one rare earth cation), ReAl₁₁O₁₈, Re₃Al₅O₁₂, Y₃Al₅O₁₂, etc. phases takes place at temperatures above about 925° C. Typically, crystallite size during this nucleation step is on order of nanometers. For example, crystals as small as 10-15 nanometers have been observed. For at least some embodiments, heat-treatment at about 1300° C. for about 1 hour provides a full crystallization. In general, heat-treatment times for each of the nucleation and crystal growth steps may range of a few seconds (in some embodiments even less than 5 seconds) to several minutes to an hour or more.

The size of the resulting crystals can typically be controlled at least in part by the nucleation and/or crystallization times and/or temperatures. Although it is generally preferred to have small crystals (e.g., on the order not greater than a micrometer, or even not greater than a nanometer), glass-ceramics may be made with larger crystal sizes (e.g., at least 1-10 micrometers, at least 10-25 micrometers, at least 50-100 micrometers, or even grater than 100 micrometers). Although not wanting to be bound by theory, it is generally believed in the art that the finer the size of the crystals (for the same density), the higher the mechanical properties (e.g., hardness and strength) of the ceramic. It is also within the scope of this invention to perform crystallization in such a manner that crystals with needle, whisker or platelet-like morphologies form during heat-treatment. Such crystals could favorably affect fracture toughness, machinability, and other characteristics of the resultant glass-ceramic.

Examples of crystalline phases which may be present in embodiments of glass-ceramics include: Al₂O₃ (e.g., α-Al₂O₃, or transitional Al₂O₃), Y₂O₃, REO, HfO₂, ZrO₂ (e.g., cubic ZrO₂ and tetragonal ZrO₂), BaO, CaO, Cr₂O₃, CoO, Fe₂O₃, GeO₂, Li₂O, MgO, MnO, NiO, Na₂O, P₂O₅, Sc₂O₃, SiO₂, SrO, TeO₂, TiO₂, V₂O₃, Y₂O₃, ZnO, “complex metal oxides” (including “complex Al₂O₃.metal oxide (e.g., complex Al₂O₃ REO (e.g., ReAlO₃ (e.g., GdAlO₃ LaAlO₃), ReAl₁₁O₁₈ (e.g., LaAl₁₁O₁₈), and Re₃Al₅O₁₂ (e.g., Dy₃Al₅O₁₂)), complex Al₂O₃—Y₂O₃ (e.g., Y₃Al₅O₁₂), and complex ZrO₂.REO (e.g., Re₂Zr₂O₇ (e.g., La₂Zr₂O₇))), and combinations thereof.

It is also within the scope of the present invention to substitute a portion of the yttrium and/or aluminum cations in a complex Al₂O₃.metal oxide (e.g., complex Al₂O₃—Y₂O₃ (e.g., yttrium aluminate exhibiting a garnet crystal structure)) with other cations. For example, a portion of the Al cations in a complex Al₂O₃.Y₂O₃ may be substituted with at least one cation of an element selected from the group consisting of: Cr, Ti, Sc, Fe, Mg, Ca, Si, Co, and combinations thereof. For example, a portion of the Y cations in a complex Al₂O₃.Y₂O₃ may be substituted with at least one cation of an element selected from the group consisting of: Ce, Dy, Er, Eu, Gd, Ho, La, Lu, Nd, Pr, Sm, Th, Tm, Yb, Fe, Ti, Mn, V, Cr, Co, Ni, Cu, Mg, Ca, Sr, and combinations thereof. Similarly, it is also within the scope of the present invention to substitute a portion of the aluminum cations in alumina. For example, Cr, Ti, Sc, Fe, Mg, Ca, Si, and Co can substitute for aluminum in the alumina. The substitution of cations as described above may affect the properties (e.g., hardness, toughness, strength, thermal conductivity, etc.) of the fused material.

It is also within the scope of the present invention to substitute a portion of the rare earth and/or aluminum cations in a complex Al₂O₃.metal oxide (e.g., complex Al₂O₃.REO) with other cations. For example, a portion of the Al cations in a complex Al₂O₃.REO may be substituted with at least one cation of an element selected from the group consisting of: Cr, Ti, Sc, Fe, Mg, Ca, Si, Co, and combinations thereof. For example, a portion of the Y cations in a complex Al₂O₃.REO may be substituted with at least one cation of an element selected from the group consisting of: Y, Fe, Ti, Mn, V, Cr, Co, Ni, Cu, Mg, Ca, Sr, and combinations thereof. Similarly, it is also within the scope of the present invention to substitute a portion of the aluminum cations in alumina. For example, Cr, Ti, Sc, Fe, Mg, Ca, Si, and Co can substitute for aluminum in the alumina. The substitution of cations as described above may affect the properties (e.g., hardness, toughness, strength, thermal conductivity, etc.) of the fused material.

The average crystal size can be determined by the line intercept method according to the ASTM Standard E 112-96 “Standard Test Methods for Determining Average Grain Size”. The sample is mounted in mounting resin (such as that obtained under the trade designation “TRANSOPTIC POWDER” from Buehler Ltd., Lake Bluff, Ill.) typically in a cylinder of resin about 2.5 cm in diameter and about 1.9 cm high. The mounted section is prepared using conventional polishing techniques using a polisher (such as that obtained from Buehler Ltd., Lake Bluff, Ill., under the trade designation “ECOMET 3”). The sample is polished for about 3 minutes with a diamond wheel, followed by 5 minutes of polishing with each of 45, 30, 15, 9, 3, and 1-micrometer slurries. The mounted and polished sample is sputtered with a thin layer of gold-palladium and viewed using a scanning electron microscopy (such as the JEOL SEM Model JSM 840A). A typical back-scattered electron (BSE) micrograph of the microstructure found in the sample is used to determine the average crystal size as follows. The number of crystals that intersect per unit length (NL) of a random straight line drawn across the micrograph are counted. The average crystal size is determined from this number using the following equation: ${{Average}\quad{Crystal}\quad{Size}} = \frac{1.5}{N_{L}M}$

Where N_(L) is the number of crystals intersected per unit length and M is the magnification of the micrograph.

Some embodiments of the present invention include glass-ceramics comprising crystals having at least one of an average crystal size not greater than 150 nanometers.

Some embodiments of the present invention include glass-ceramics comprising crystals, wherein at least 90 (in some embodiments preferably, 95, or even 100) percent by number of the crystals present in such portion have crystal sizes not greater than 200 nanometers.

Some embodiments of the present invention include glass-ceramics comprising Al₂O₃, and a first complex Al₂O₃—Y₂O₃, and optionally crystalline ZrO₂, and wherein at least one of the Al₂O₃, the optional crystalline ZrO₂, or the first complex Al₂O₃.Y₂O₃ has an average crystal size not greater than 150 nanometers. In some embodiments preferably, the glass-ceramics further comprise a second, different complex Al₂O₃.Y₂O₃. In some embodiments preferably, the glass-ceramics further comprise a complex Al₂O₃.REO. Some embodiments of the present invention include glass-ceramics comprising a first complex Al₂O₃—Y₂O₃, a second, different complex Al₂O₃—Y₂O₃, and optionally crystalline ZrO₂, and wherein for at least one of the first complex Al₂O₃.Y₂O₃, the second complex Al₂O₃.Y₂O₃, or the optional crystalline ZrO₂, at least 90 (in some embodiments preferably, 95, or even 100) percent by number of the crystal sizes thereof are not greater than 200 nanometers. In some embodiments preferably, the glass-ceramics further comprise a second, different complex Al₂O₃—Y₂O₃. In some embodiments preferably, the glass-ceramics further comprise a complex Al₂O₃.REO.

Some embodiments of the present invention include glass-ceramics comprising Al₂O₃, a first complex Al₂O₃.REO, and optionally crystalline ZrO₂, and wherein at least one of the Al₂O₃, the optional crystalline ZrO₂, or the first complex Al₂O₃.REO has an average crystal size not greater than 150 nanometers. In some embodiments preferably, the glass-ceramics further comprise a second, different complex Al₂O₃.REO. In some embodiments preferably, the glass-ceramics further comprise a complex Al₂O₃.Y₂O₃.

Some embodiments of the present invention include glass-ceramics comprising a first complex Al₂O₃.REO, a second, different complex Al₂O₃.REO, and optionally crystalline ZrO₂, and wherein for at least one of the first complex Al₂O₃.REO, the second complex Al₂O₃.REO, or the optional crystalline ZrO₂, at least 90 (in some embodiments preferably, 95, or even 100) percent by number of the crystal sizes thereof are not greater than 200 nanometers. In some embodiments preferably, the glass-ceramics further comprise a complex Al₂O₃.Y₂O₃.

In some embodiments, glass-ceramics comprise at least 75, 80, 85, 90, 95, 97, 98, 99, or even 100 percent by volume crystallites, wherein the crystallites have an average size of less than 1 micrometer. In some embodiments, glass-ceramics comprise not greater than at least 75, 80, 85, 90, 95, 97, 98, 99, or even 100 percent by volume crystallites, wherein the crystallites have an average size not greater than 0.5 micrometer. In some embodiments, glass-ceramics comprise less than at 75, 80, 85, 90, 95, 97, 98, 99, or even 100 percent by volume crystallites, wherein the crystallites have an average size not greater than 0.3 micrometer. In some embodiments, glass-ceramics comprise less than at least 75, 80, 85, 90, 95, 97, 98, 99, or even 100 percent by volume crystallites, wherein the crystallites have an average size not greater than 0.15 micrometer.

Crystals formed by heat-treating amorphous to provide embodiments of glass-ceramics may be, for example, equiaxed, columnar, or flattened splat-like. The aspect ratio and overall size of whisker, needle, or platelet-like crystals may be optionally controlled to improve properties.

Although a glass-ceramic may be in the form of a bulk material, it is also within the scope of the present invention to provide composites comprising a glass-ceramic. Such a composite may comprise, for example, a phase or fibers (continuous or discontinuous) or particles (including whiskers) (e.g., metal oxide particles, boride particles, carbide particles, nitride particles, diamond particles, metallic particles, glass particles, and combinations thereof) dispersed in a glass-ceramic, invention or a layered-composite structure (e.g., a gradient of glass-ceramic to amorphous material used to make the glass-ceramic and/or layers of different compositions of glass-ceramics).

Typically, the (true) density, sometimes referred to as specific gravity, of ceramics is typically at least 70% of theoretical density. More desirably, the (true) density of ceramic is at least 75%, 80%, 85%, 90%, 92%, 95%, 96%, 97%, 98%, 99%, 99.5%, or even 100% of theoretical density.

The average hardness of the material of the present invention can be determined as follows. Sections of the material are mounted in mounting resin (obtained under the trade designation “TRANSOPTIC POWDER” from Buehler Ltd., Lake Bluff, Ill.) typically in a cylinder of resin about 2.5 cm in diameter and about 1.9 cm high. The mounted section is prepared using conventional polishing techniques using a polisher (such as that obtained from Buehler Ltd., Lake Bluff, Ill., under the trade designation “ECOMET 3”). The sample is polished for about 3 minutes with a diamond wheel, followed by 5 minutes of polishing with each of 45, 30, 15, 9, 3, and 1-micrometer slurries. The microhardness measurements are made using a conventional microhardness tester (such as that obtained under the trade designation “MITUTOYO MVK-VL” from Mitutoyo Corporation, Tokyo, Japan) fitted with a Vickers indenter using a 100-gram indent load. The microhardness measurements are made according to the guidelines stated in ASTM Test Method E384 Test Methods for Microhardness of Materials (1991), the disclosure of which is incorporated herein by reference.

Additional glasses and glass-ceramics, methods of making same, and methods of making articles containing same, which may be useful in the articles and methods according to the present invention include those disclosed in applications having U.S. application Ser. Nos. 09/922,526, 09/922,527, 09/922,528, and 09/922,530, filed Aug. 2, 2001, now abandoned; U.S. application Ser. Nos. 10/211,491, filed Aug. 2, 2002; U.S. application Ser. Nos. 10/358,910, 10/358,708, 10/358,855, 10/358,772, and 10/358,765, each filed Feb. 5, 2003; and U.S. Publication Nos. 04-0023078-A1, 04-0020245-A1, 03-0126803-A1, 03-0110708-A1, 03-0110706-A1, 03-0115805-A1, 03-0110707-A1, 03-0110709-A1, 03-0126802-A1, 03-0145525-A1, and 03-0126804-A1, the disclosures of which are incorporated herein by reference.

Dental Materials

The ceramics, glass, and glass-ceramics described above can be incorporated into a hardenable resin to provide useful dental or orthodontic materials such as a paste. These resins are generally thermosetting materials capable of being hardened to form a polymer network including, for example, acrylate-functional materials, methacrylate-functional materials, epoxy-functional materials, vinyl-functional materials, and mixtures thereof. Suitably, the hardenable resin is made from one or more matrix-forming oligomer, monomer, polymer, or blend thereof.

Hardenable resins suitable for use in the dental materials of the present invention include hardenable organic materials having sufficient strength, hydrolytic stability, and non-toxicity to render them suitable for use in the oral environment. Examples of such materials include acrylates, methacrylates, urethanes, carbamoylisocyanurates, epoxies (e.g., those shown in U.S. Pat. No. 3,066,112 (Bowen); U.S. Pat. No. 3,539,533 (Lee II et al.); U.S. Pat. No. 3,629,187 (Waller); U.S. Pat. No. 3,709,866 (Waller); U.S. Pat. No. 3,751,399 (Lee et al.); U.S. Pat. No. 3,766,132 (Lee et al.); U.S. Pat. No. 3,860,556 (Taylor); U.S. Pat. No. 4,002,669 (Gross et al.); U.S. Pat. No. 4,115,346 (Gross et al.); U.S. Pat. No. 4,259,117 (Yamauchi et al.); U.S. Pat. No. 4,292,029 (Craig et al.); U.S. Pat. No. 4,308,190 (Walkowiak et al.); U.S. Pat. No. 4,327,014 (Kawahara et al.); U.S. Pat. No. 4,379,695 (Orlowski et al.); U.S. Pat. No. 4,387,240 (Berg); U.S. Pat. No. 4,404,150 (Tsunekawa et al.)); and mixtures and derivatives thereof.

One class of preferred hardenable materials includes materials having free radically active functional groups. Examples of such materials include monomers having one or more ethylenically unsaturated group, oligomers having one or more ethylenically unsaturated group, polymers having one or more ethylenically unsaturated group, and combinations thereof. Alternatively, the hardenable resin can be selected from materials that include cationically active functional groups. In another alternative, a mixture of hardenable resins that include both cationically curable and free radically curable materials may be used for the dental materials of the invention. In another alternative, the hardenable resin can be a material from the class of materials that includes both cationically active and free radically active functional groups in the same molecule.

In the class of hardenable resins having free radically active functional groups, suitable materials for use in the invention contain at least one ethylenically unsaturated bond, and are capable of undergoing addition polymerization. Such free radically polymerizable materials include mono-, di- or poly-acrylates and methacrylates such as methyl acrylate, methyl methacrylate, ethyl acrylate, isopropyl methacrylate, n-hexyl acrylate, stearyl acrylate, allyl acrylate, glycerol diacrylate, glycerol triacrylate, ethyleneglycol diacrylate, diethyleneglycol diacrylate, triethyleneglycol dimethacrylate, 1,3-propanediol diacrylate, 1,3-propanediol dimethacrylate, trimethylolpropane triacrylate, 1,2,4-butanetriol trimethacrylate, 1,4-cyclohexanediol diacrylate, pentaerythritol triacrylate, pentaerythritol tetraacrylate, pentaerythritol tetramethacrylate, sorbitol hexacrylate, the diglycidyl methacrylate of bis-phenol A (“Bis-GMA”), bis[1-(2-acryloxy)]-p-ethoxyphenyldimethylmethane, bis[1-(3-acryloxy-2-hydroxy)]-p-propoxyphenyldimethylmethane, and trishydroxyethyl-isocyanurate trimethacrylate; the bis-acrylates and bis-methacrylates of polyethylene glycols of molecular weight 200-500, copolymerizable mixtures of acrylated monomers such as those in U.S. Pat. No. 4,652,274 (Boettcher et al.), and acrylated oligomers such as those of U.S. Pat. No. 4,642,126 (Zador); and vinyl compounds such as styrene, diallyl phthalate, divinyl succinate, divinyl adipate and divinylphthalate. Mixtures of two or more of these free radically polymerizable materials can be used if desired.

For free radical polymerization (e.g., hardening), an initiation system can be selected from systems that initiate polymerization via radiation, heat, or redox/auto-cure chemical reaction. A class of initiators capable of initiating polymerization of free radically active functional groups includes free radical-generating photoinitiators, optionally combined with a photosensitizer or accelerator. Such initiators typically can be capable of generating free radicals for addition polymerization upon exposure to light energy having a wavelength between 200 and 800 nm.

A variety of visible or near-IR photoinitiator systems may be used for photopolymerization of free-radically polymerizable materials. For example, a photoinitiation system can be selected from systems which initiate polymerization via a two component system of an amine and an α-diketone as described in U.S. Pat. No. 4,071,424 (Dart et al.). Alternatively, the material can be combined with a three component photoinitiator system such as described in U.S. Pat. No. 5,545,676 (Palazzotto et al.). The three component system includes an iodonium salt (e.g., a diaryliodonium salt), a sensitizer, and a donor. Each photoinitiator component is described in U.S. Pat. No. 5,545,676, column 2, line 27, to column 4, line 45.

Other useful free-radical initiators include the class of acylphosphine oxides, as described in European Pat. Application Publ. No. 173,567 (Ying) and U.S. Pat. No. 4,737,593 (Ellrich et al.) and U.S. Pat. No. 6,020,528 (Leppard et al.). Tertiary amine reducing agents may be used in combination with an acylphosphine oxide.

Another free-radical initiator system that can alternatively be used in the dental materials of the invention includes the class of ionic dye-counterion complex initiators including a borate anion and a complementary cationic dye. Borate salt photoinitiators are described, for example, in U.S. Pat. No. 4,772,530 (Gottschalk et al.); U.S. Pat. No. 4,954,414 (Adair et al.); U.S. Pat. No. 4,874,450 (Gottschalk); U.S. Pat. No. 5,055,372 (Shanklin et al.); and U.S. Pat. No. 5,057,393 (Shanklin et al.).

Yet another alternative class of initiators capable of initiating polymerization of free radically active functional groups in the hardenable resin includes conventional chemical initiator systems such as a combination of a peroxide and an amine. These initiators, which rely upon a thermal redox reaction, are often referred to as “auto-cure catalysts.” They are typically supplied as two-part systems in which the reactants are stored apart from each other and then combined immediately prior to use.

In a further alternative, heat may be used to initiate the hardening, or polymerization, of free radically active groups. Examples of heat sources suitable for the dental materials of the invention include inductive, convective, and radiant. Thermal sources should be capable of generating temperatures of at least about 40° C. and at most about 150° C. under normal conditions or at elevated pressure. This procedure is preferred for initiating polymerization of materials occurring outside of the oral environment.

Yet another alternative class of initiators capable of initiating polymerization of free radically active functional groups in the hardenable resin are those that include free radical-generating thermal initiators. Examples include peroxides (e.g., benzoyl peroxide and lauryl peroxide) and azo compounds (e.g., 2,2-azobis-isobutyronitrile (AIBN)).

An alternative class of hardenable resins useful in dental materials disclosed in the present application includes materials having cationically active functional groups. Materials having cationically active functional groups include cationically polymerizable epoxies, vinyl ethers, oxetanes, spiro-orthocarbonates, spiro-orthoesters, and the like. Preferred materials having cationically active functional groups are epoxy-functional materials including, for example, those disclosed in U.S. Pat. No. 6,025,406 (Oxman et al.) (e.g., column 2, line 36, to column 4, line 52) and in the documents cited therein.

Optionally, monohydroxy- and polyhydroxy-alcohols may be added to the hardenable resin, as chain-extenders for a hardenable resin having cationically active functional groups, which are preferably epoxy-functional materials. The hydroxyl-containing material used in the present invention can be any organic material having hydroxyl functionality of at least about 1, and preferably at least about 2. Useful hydroxyl-containing materials are described, for example, in U.S. Pat. No. 5,856,373 (Kaisaki et al.).

For hardening resins including cationically active functional groups, an initiation system can be selected from systems that initiate polymerization via radiation, heat, or redox/auto-cure chemical reactions. For example, epoxy polymerization may be accomplished by the use of thermal curing agents including, for example, anhydrides and amines. A particularly useful example of an anhydride curing agent is cis-1,2-cyclohexanedicarboxylic anhydride.

Alternatively, initiation systems for resins including cationically active functional groups are those that are photoactivated. The broad class of cationic photoactive groups recognized in the catalyst and photoinitiator industries may be used in the practice of the present invention. Photoactive cationic nuclei, photoactive cationic moieties, and photoactive cationic organic compounds are art recognized classes of materials as exemplified by, for example, U.S. Pat. No. 4,250,311 (Crivello); U.S. Pat. No. 3,708,296 (Schlesinger); U.S. Pat. No. 4,069,055 (Crivello); U.S. Pat. No. 4,216,288 (Crivello); U.S. Pat. No. 5,084,586 (Farooq); U.S. Pat. No. 5,124,417 (Farooq); U.S. Pat. No. 4,985,340 (Palazzotto et al.); U.S. Pat. No. 5,089,536 (Palazzotto); and U.S. Pat. No. 5,856,373 (Kaisaki et al.).

The cationically-curable materials can be combined with a three component or ternary photoinitiator system, as described above, for example, using an iodonium salt, a sensitizer, and an electron donor. For hardening cationically curable materials, examples of useful aromatic iodonium complex salts are disclosed in U.S. Pat. No. 6,025,406 (Oxman et al.) (e.g., column 5, line 46, to column 6, line 9). Examples of useful sensitizers and electron donors can also be found in U.S. Pat. No. 6,025,406 (e.g., column 6, line 43, to column 9, line 43).

An alternative photoinitiator system for cationic polymerizations includes the use of organometallic complex cations essentially free of metal hydride or metal alkyl functionality selected from those described in U.S. Pat. No. 4,985,340 (Palazzotto et al.).

Alternatively, the hardenable resins may have both cationically active and free radically active functional groups contained in a single molecule. Such molecules may be obtained, for example, by reacting a di- or poly-epoxide with one or more equivalents of an ethylenically unsaturated carboxylic acid. An example of such a material is the reaction product of a material, which is available under the trade designation “UVR-6105” from Union Carbide, with one equivalent of methacrylic acid. Commercially available materials having epoxy and free-radically active functionalities include materials available under the trade designation “CYCLOMER” (e.g., “CYCLOMER M-100”, “M-101”, or “A-200”) from Daicel Chemical, Japan, and the material available under the trade designation “EBECRYL-3605” from Radcure Specialties.

Photoinitiator compounds are preferably provided in dental materials disclosed in the present application in an amount effective to initiate or enhance the rate of cure or hardening of the resin system. Useful photopolymerizable compositions are prepared by simply admixing, under safe light conditions, the components as described above. Suitable inert solvents may be used, if desired, when preparing this mixture. Any solvent that does not react appreciably with the components of the inventive compositions may be used. Examples of suitable solvents include, for example, acetone, dichloromethane, and acetonitrile. A liquid material to be polymerized may be used as a solvent for another liquid or solid material to be polymerized. Solventless compositions can be prepared, for example, by simply dissolving an aromatic iodonium complex salt and sensitizer in an epoxy-functional material/polyol mixture with or without the use of mild heating to facilitate dissolution.

An additional class of hardenable resins include those with pendant acid moieties, which can undergo a setting reaction in the presence of reactive fillers and water. Examples of suitable acid moieties include carboxylates, phosphates, and phosphonates. Examples of suitable compounds include polyacrylic acid; polymers derived from the acrylic acid, methacrylic acid, itaconic acid, maleic acid, glutaconic acid, aconitic acid, citraconic acid, mesaconic acid, fumaric acid, tiglic acid, and combinations thereof; glycerol dimethacrylate phosphate; citric acid dimethacrylate; and propionic acid dimethacrylate and combinations thereof.

The dental materials of the invention may optionally include adjuvants suitable for use in the oral environment including, for example, colorants, flavorants, anti-microbials, fragrances, stabilizers, viscosity modifiers, and fluoride releasing materials. For example, a fluoride releasing glass may be added to dental materials or glasses of the present invention to provide the benefit of long-term release of fluoride in use, for example in the oral cavity. Fluoroaluminosilicate glasses are particularly preferred. Particularly preferred fluoroaluminosilicate glasses are those that have been silanol treated as described, for example, in U.S. Pat. No. 5,332,429 (Mitra et al.). Other suitable adjuvants include, for example, agents that impart fluorescence and/or opalescence.

Method of Making

In one embodiment of the present invention, dental or orthodontic materials are made by mixing a glass, glass-ceramic, or ceramic with a hardenable resin. The dental materials may be provided in various containers including capsules, syringes, foli packages, and cartridges. Dental articles and orthodontic appliances may then be made by forming the dental or orthodontic material into the desired shape and then hardening the hardenable resin.

Typically, the dental material is initially a viscous material, for example, paste, and any of the standard methods for compounding paste may be used to form the composite material. Usually, methods which optimize mixing and minimize the incidence of material discontinuities such as voids and cracks should be instituted. For example, application of vacuum or pressure can be beneficial during any stage of compounding, forming, or curing the paste. Pressure can be applied by various means, including isostatic, uniaxial, centrifugal, impact, or pressurized gas. Heat may optionally be applied at any stage. However, during curing, a uniform temperature in the sample is preferably maintained to minimize internal stresses. During compounding and extrusion, methods that minimize and preferably eliminate material discontinuities such as voids or bubbles are preferred.

Mill blanks of dental or orthodontic material may be made in any desired shape or size, including cylinders, bars, cubes, polyhedra, ovoids, and plates as is known in the art. Molds may be made of a variety of materials, including stainless steel, cobalt alloys, nickel alloys, aluminum alloys, plastic, glass, ceramic, or combinations thereof. Alternatively, a variety of methods for forming and shaping the blanks into any desired configuration can be employed, such as injection molding, centrifugal casting and extrusion. During hardening, compression from springs or other means may optionally be used to reduce internal stresses. Preferably, the outer surface of the blank is smooth and non-tacky.

Hardening may be performed in one or multiple stage methods. In a two-stage process, it is preferred that initial hardening provide a material sufficient to sustain the forces of milling or carving. The second hardening stage, therefore, can be performed on the composite after a dental article or orthodontic appliance is milled from a blank or molded. Such blanks are described in, for example, PCT Publication No. WO 01/13862 A1, incorporated by reference herein.

Hardened blocks may be attached to mounting stubs to facilitate affixation of the blank in a milling machine. Mounting stubs function as handles from which a blank is held by as it is milled by a machine.

Various means of milling the mill blanks of the present invention may be employed to create custom-fit dental prosthetics having a desired shape and morphology. The term “milling” as used herein means abrading, polishing, controlled vaporization, electronic discharge milling (EDM), cutting by water jet or laser or any other method of cutting, removing, shaping, or carving material. While milling the blank by hand using a hand-held tool or instrument is possible, preferably the prosthetic is milled by machine, including computer controlled milling equipment. However, a preferred device to create a prosthetic and achieve the full benefits of the composite material of the present invention is to use a CAD/CAM device capable of milling a blank, such as the Sirona Cerec 2 machine. By using a CAD/CAM milling device, the prosthetic can be fabricated efficiently and with precision. During milling, the contact area may be dry, or it may be flushed with a lubricant. Alternatively, it may be flushed with an air or gas stream. Suitable lubricants are well known in the art, and include water, oils, glycerine, ethylene glycols, and silicones. After machine milling, some degree of finishing, polishing, and adjustment may be necessary to obtain a custom fit in to the mouth and/or aesthetic appearance.

To fabricate blanks of the present invention, the following steps are typically performed: Compound the paste; extrude the paste into a mold; cure the paste via heat, light, microwave, e-beam or chemical cure; remove the blank from its mold and trim excess if necessary; and optionally, mount on a holder stub if necessary. An exemplary method of making the dental mill blank of the present invention comprises the steps of a) mixing a paste comprising a resin and a filler, b) shaping the paste into a desired configuration, c) minimizing material discontinuities from the paste, d) curing the paste into a blank, and e) relieving internal stresses in the blank.

Optionally, where a mold is used to shape the paste, excess paste material can be trimmed from the mold. The cured paste is then removed from the mold. Another optional step that can be performed in making a mill blank is to mount a handle onto the cured paste. Preferably, the handle is a holder stub.

Mill blanks of the present invention may be hardened in a manner such that the material contains minimal internal stresses. This may be accomplished, for example, by application of pressure on the composite material during the hardening process. In the alternative, the avoidance of internal stress imparted by shrinkage may be obtained by selection of mill blank components such that the overall composition exhibits little or no shrinkage during hardening. A preferred curing method entails the use of light to fast harden the composite. During this fast hardening, the temperature may optionally be adjusted and controlled. The fast hardening technique requires a subsequent heat treatment to effectuate stress relief. Heat treatment of a hardened blank requires the blank be heated for a sufficient time and at a sufficient temperature to effectively eliminate internal stresses such that the blank passes a Thermal Shock Test. Preferably, the blank is raised to a temperature of at or above T_(g) (glass transition temperature) of the resin component of the blank. More preferably, the blank is heated to above T_(g) and is maintained at that temperature for at least about one-half hour.

An exemplary method of heat treatment for a hardened blank is to place the blank in an oven and raise the oven temperature to about the T_(g) of the resin component of the blank at a rate of about, for example, 3-5° C./minute. Upon completing heat treatment, the blank is allowed to equilibrate to room temperature either by immersion into room temperature water or by slowly cooling via ambient temperature. Alternatively, the heat treatment may be accomplished by placing the blank in a preheated oven and maintaining the oven temperature at or above T_(g) for a sufficient time to eliminate internal stresses in the composite blank.

Another method of curing the blanks of the present invention is through a slow hardening using low intensity light. In this technique, hardening is accomplished over a long period of time to minimize internal stresses, such that the resulting hardened blank will pass a Thermal Shock Test. Preferably, the hardening takes place over a time period of about 24 hours, however, it is envisioned that with proper equipment and procedure, curing times may be shorter. Progress of this hardening may be evaluated by ascertaining a sample of the material at predetermined times over the hardening time and evaluating progress of hardening by Barcol Hardness measurement.

Other techniques may be used to relieve the stress of mill blanks of the present invention, including application of energy in a form other than heat, such as sonic or microwave energy.

The ceramics, glasses, and glass-ceramics described in the present application are useful in making dental articles and orthodontic appliances that comprise said ceramics, glasses, and glass-ceramics, as described herein. The ceramics, glasses, and glass-ceramics described herein may be formed, molded, shaped, pressed, etc. into the form of dental articles and orthodontic appliances.

In one embodiment, a method of making a dental article or orthodontic appliance comprises the steps of optionally designing the dental article or the orthodontic appliance; carving a dental or orthodontic mill blank based on said optional design, wherein the dental mill blank comprises a ceramic comprising at least one of the glasses or glass-ceramics described herein. The mill blank or the dental article or orthodontic appliance may be further heat treated as described herein.

In another embodiment, a method of making a dental article or an orthodontic appliance comprising the steps of designing the dental article or the orthodontic appliance, heating a glass above the T_(g) of the glass such that the glass coalesce (or forms, in the case of a perform) to form a dental article or an orthodontic appliance having a shape based on said optional design; and cooling the coalesced article, wherein the glass comprises at least one of the glasses described herein. The coalesced article may be further heat treated to form an article comprising glass-ceramic. The glass may be in the form of particles, powder, nanoclusters, fibers, flakes, whiskers, block, blank, beads, etc., or combinations thereof.

In another embodiment, a method of making a dental article or orthodontic appliance comprise the steps of optionally designing the dental article or the orthodontic appliance; combining a ceramic, glass, or glass-ceramic with a hardenable resin to form a mixture; forming the dental article or the orthodontic appliance into a shape based on said optional design; hardening said mixture to form the dental article or orthodontic appliance, wherein said ceramic comprises at least one of the glasses, or glass-ceramics described herein.

In another embodiment, the invention provides a method of making a dental article or orthodontic appliance comprising the steps of plasma or thermally spraying particles comprising metal oxide sources onto a suitable substrate such that the particles coalesce to form a shaped article and optionally separating the shaped article or appliance from the substrate, wherein the shaped article comprises at least one of the glasses described herein. Useful substrates include refractory materials that comprise admixtures of silica, silicon carbide, magnesium oxide, mono ammonium phosphate, zircon or aluminum oxide. Metal substrates can also be used in some embodiments.

Uses

The dental materials, glasses, ceramics, and glass-ceramics disclosed in the present application can be used, for example, as dental adhesives, artificial crowns, anterior or posterior fillings, casting materials, cavity liners, pastes, cements, coating compositions, mill blanks, orthodontic appliances, dental articles, restoratives, prostheses, and sealants. For example, restoratives of the invention can be placed directly in the mouth, shaped or formed, and cured (hardened) in-situ, or alternatively, may be fabricated into a prosthesis outside the mouth and subsequently adhered in place inside the mouth.

Practitioners generally desire handling properties in a dental material that allows fast and easy placement, which often translates to time savings. For example, in dental restorative work, it is desirable in some instances that dental materials do not slump (e.g., flow or change in shape), because after a practitioner places the material in the mouth and manipulates the material by contouring and feathering, the practitioner generally wants the imparted shape to remain unchanged until the material is hardened. Materials used for restorative work, having a sufficiently high yield stress generally will not slump; that is, they will not flow under the stress of gravity. The yield stress of a material is the minimum stress required to cause the material to flow, and is described in “Rheology Principles, Measurements, and Applications” by C. W. Macosko, VCH Publishers, Inc., New York, 1994, p. 92. If the stress due to gravity is below the yield stress of the material, then the material will not flow. The stress due to gravity, however, will depend on the mass of dental material being placed as well as the shape.

“Contouring” refers to the process of shaping a material (using dental instruments) so that it resembles the natural dental anatomy. For easy contouring, materials should have a sufficiently high viscosity that they maintain their shape after manipulation with a dental instrument, and yet the viscosity should not be so high that it is difficult to shape the material. “Feathering” refers to the process of reducing the dental material to a thin film in order to blend the material into the natural dentition. This is done with a dental instrument at the margin of the manipulated material and the natural dentition. It is also desirable that the dental material not stick to placement instruments, to minimize further alteration of the shape or surface topography.

In an embodiment where the dental material of the invention is a restorative, the dental material preferably has little to no slump, yet easily adapts to, for example, a cavity preparation, and is easily contoured and feathered. Preferably, the dental materials of the invention do not stick to placement instruments, and are advantageously, overall, fast and easy to use in dental procedures such as, for example, restoring tooth structure.

In certain embodiments, the present invention provides dental materials that are capable of being hardened to provide a balance of desirable properties as detailed below (e.g., a low opacity, a low volumetric shrinkage value, a high diametral tensile strength, a high compressive strength, a high retention of gloss upon polishing).

The dental materials of the present invention may be hardened to form, for example, dental articles and orthodontic appliances. In a method of using dental materials including a hardenable resin and ceramics as disclosed in the present application, the dental material may be placed near or on a tooth surface, followed by a manipulation by the practitioner or laboratory to change the topography of the material, then the resin may be hardened. These steps can be followed sequentially or in a different order. For example, where the dental material is a mill blank or an article or appliance, the hardening step is generally completed prior to changing the topography of the dental material. Changing the topography of the dental material can be accomplished in various ways including, for example, carving or manual manipulation using hand held instruments, or by machine or computer aided apparatus (e.g., a CAD/CAM milling machine) in the case of prostheses and mill blanks. Optionally, a finishing step can be performed to polish, finish, or apply a coating on the dental article.

A dental article or orthodontic appliance can be attached to the tooth or bone structure with conventional cements or adhesives or other appropriate means such as glass ionomer, resin cement, zinc phosphate, zinc polycarboxylate, compomer, or resin-modified glass. In addition, material can optionally be added to the milled article or appliance for various purposes including repair, correction, or enhancing esthetics. The additional material may be of one or more different shades or colors. The added material may be composite, ceramic, or metal. A dental porcelain or light-cured composite is preferred.

Strength can be characterized by mechanical measurements such as compressive strength (CS) and diametral tensile strength (DTS). High compressive strength in a dental material is advantageous due to the forces exerted by mastication on dental repairs, replacements, and restorations. Some embodiments of the dental articles and orthodontic appliances disclosed in the present application may exhibit desirable aesthetic qualities including high translucency, high gloss, and high retention of polish after exposure to repetitive abrasion.

Aesthetic quality of a dental article or orthodontic appliance, although a somewhat subjective characteristic (yet well-understood in the dental industry), can be preferably quantified in one aspect, by measuring MacBeth values, in which lower MacBeth values indicate a lower visual opacity. Visual opacity is indicative of dental article's or orthodontic appliance's level of translucency. Low visual opacity is desired so that the hardened dental material will have a life-like luster.

High translucency of a dental article or orthodontic appliance contributes to the aesthetic character and quality of the material. Polishability of such articles and appliances also contributes to the aesthetic character and quality of the material. The ability of such articles and appliances to have a glossy finish and life-like luster upon polishing is highly desirable. An even greater benefit is the ability of such articles and appliances to retain their luster even after repetitive abrasive contact, such as tooth brushing. It has been surprisingly found that some embodiments of dental articles and orthodontic appliances disclosed in the present application have high polishability and are able to retain the polish and luster after repetitive tooth brushing.

The dental materials, dental articles, and orthodontic appliances of the invention can be incorporated into kits, wherein at least one of the articles or appliances is a dental material, dental article or orthodontic appliance of the invention. The kits may also include one or more other components such as a dental mill blank, a bonding agent, a milling lubricant, a color-matching composition suitable for using in an oral environment, an impression material, an instrument, a dental composite, a paste, a dental porcelain, an abrasive, an orthodontic adhesive, an adhesive primer, an appliance positioning tool, instructions for the use of any of these components alone or in combination with any other component or components, and combinations thereof.

Other uses of the ceramics, glasses, and glass-ceramics described herein are as reactive fillers for use in glass ionomers cement as described in U.S. Pat. No. 6,136,885, PCT Publication No. WO 02/085313, and U.S. Pat. No. 5,130,347, incorporated by reference herein; as materials for dental restorations applied by flame spraying as described in U.S. Pat. No. 6,938,990 B1, incorporated by reference herein; in the forming methods described in U.S. Pat. No. 6,342,458 B1, incorporated by reference herein; as dental mill blanks as described in U.S. Pat. No. 6,394,880, incorporated by reference herein; as a porous material for glass infiltration as described in U.S. Pat. Nos. 5,910,273 and 5,250,352, incorporated by reference herein.

EXAMPLES

Raw materials used to make the amorphous glass beads in the Examples were obtained from the following sources unless otherwise indicated Raw Material Source Alumina powder (Al₂O₃) Obtained from Condea Vista, Tucson, AZ, under the trade designation “APA-0.5” Calcium oxide powder (CaO) Obtained from Alfa Aesar, Ward Hill, MA Calcium fluoride powder (CaF₂) Obtained from Alfa Aesar Cerium oxide powder (CeO₂) Obtained from Rhone-Poulenc, France Chromium oxide powder (Cr₂O₃) Obtained from Aldrich Chemical Company, Milwaukee, WI Dysprosium oxide powder (Dy₂O₃) Obtained from Aldrich Chemical Company Erbium oxide powder (Er₂O₃) Obtained from Aldrich Chemical Company Europium oxide powder (Eu₂O₃) Obtained from Aldrich Chemical Company Gadolinium oxide powder (Gd₂O₃) Obtained from Molycorp Inc., Mountain Pass, CA Hafnium oxide powder (HfO₂) Obtained from Teledyne Wah Chang Albany Company, Albany, OR Iron oxide powder (Fe₂O₃) Obtained from Aldrich Chemical Company Lanthanum oxide powder (La₂O₃) Obtained from Molycorp Inc. Lithium carbonate powder (Li₂CO₃) Obtained from Aldrich Chemical Company Magnesium oxide powder (MgO) Obtained from Aldrich Chemical Company Manganese oxide powder (MnO) Obtained from Aldrich Chemical Company Neodymium oxide powder (Nd₂O₃) Obtained from Molycorp Inc. Niobium oxide powder (Nb₂O₅) Obtained from Aldrich Chemical Company Phosphorous oxide powder (P₂O₅) Obtained from Aldrich Chemical Company Silica powder (SiO₂) Obtained from Alfa Aesar Sodium bicarbonate powder (NaHCO₃) Obtained from Aldrich Chemical Company Strontium oxide powder (SrO) Obtained from Alfa Aesar Tantalum oxide powder (Ta₂O₅) Obtained from Aldrich Chemical Company Titanium dioxide powder (TiO₂) Obtained from Kemira Inc., Savannah, GA Yttrium oxide powder (Y₂O₃) Obtained from H.C. Stark, Newton, MA Yttria-stabilized zirconium oxide powder Obtained from Zirconia Sales, Inc., Marietta, (Y-PSZ) GA, under the trade designation “HSY-3”

Description, source, and abbreviations for the materials used to make the photocurable resins described in these Examples. Abbreviation Description Source Bis-GMA 2,2-Bis[4-(2-hydroxy-3-methacryloyloxy- Made according to propoxy)phenyl]propane (CAS No. 1565-94-2) generally accepted procedures known in the art UDMA Diurethane Dimethacrylate (CAS No. 41137-60- Rohm Tech, Inc., 4), commercially available as “ROHAMERE Malden, MA 6661-0” Bis-EMA6 Ethoxylated (6 mole ethylene oxide) Bisphenol Sartomer Co., A Dimethacrylate (CAS No. 41637-38-1), Exton, PA commercially available as “Sartomer CD541” TEGDMA Triethyleneglycol Dimethacrylate Sartomer Co. CPQ Camphorquinone Sigma-Aldrich, St. Louis, MO DPIHFP Diphenyl Iodonium Hexafluorophosphate Johnson Matthey, Alpha Aesar Division, Ward Hill, NJ EDMAB Ethyl 4-Dimethylaminobenzoate Sigma-Aldrich BHT 2,6-Di-tert-butyl-4-methylphenol Sigma-Aldrich NORBLOC 2-(2′-Hydroxy-5′-methacryloxyethylphenyl)-H- Janssen 7966 benzotriazole (CAS No. 96478-09-0) Pharmaceuticals, Titusville, PA HEMA 2-Hydroxethyl Methacrylate DeGussa Corp./Rohm America Inc.

Example 1

A polyurethane-lined mill was charged with 819.6 grams (g) of alumina particles (“APA-0.5”), 818 g of lanthanum oxide particles (obtained from Molycorp, Inc.), 362.4 g of yttria-stabilized zirconium oxide particles (with a nominal composition of 94.6 wt-% ZrO₂ (+HfO₂) and 5.4 wt-% Y₂O₃ (obtained under the trade designation “HSY-3” from Zirconia Sales, Inc. of Marietta, Ga.), 1050 g of distilled water and about 2000 g of zirconia milling media (obtained from Tosoh Ceramics, Division of Bound Brook, N.J., under the trade designation “YTZ”). The mixture was milled at 120 revolutions per minute (rpm) for 4 hours to thoroughly mix the ingredients. After the milling, the milling media were removed and the slurry was poured onto a glass (“PYREX”) pan where it was dried using a heat-gun. The dried mixture was ground with a mortar and pestle and screened through a 70-mesh screen (212-micrometer opening size). After grinding and screening, some of the particles were fed into a hydrogen/oxygen torch flame. The hydrogen torch used to melt the multiphase particles, thereby generating a melted amorphous glass bead, was a Bethlehem bench burner, delivering hydrogen and oxygen at the following rates. For the inner ring, the hydrogen flow rate was 8 standard liters per minute (SLPM), the oxygen flow rate was 3 SLPM. For the outer ring, the hydrogen flow rate was 23 standard liters per minute (SLPM), the oxygen flow rate was 9.8 SLPM. The dried and sized particles were fed directly into the hydrogen torch flame, where they were melted and transported to an inclined stainless steel surface (approximately 20 inches wide with the slope angle of 45 degrees) with cold water running over (approximately 2 L/min). Obtained in this procedure amorphous beads ranged in size from 30 to 150 microns.

About 50 g of the amorphous beads was placed in a graphite die and hot-pressed using a uniaxial pressing apparatus (obtained under the trade designation “HP-50”, Thermal Technology Inc., Brea, Calif.). The hot-pressing was carried out at 960° C. in an argon atmosphere and 13.8 megapascals (MPa) (2000 pounds per square inch (2 ksi)) pressure. The resulting disk was about 48 millimeters in diameter, and about 5 mm thick. Additional hot-press runs were performed to make additional disks. FIG. 1 is an optical photomicrograph of a sectioned bar (2-mm thick) of the hot-pressed material demonstrating its transparency.

The Young's Modulus (E) of the resulting hot-pressed glass material was measured using a ultrasonic test system (obtained from Nortek, Richland, Wash., under the trade designation “NDT-140”), and found to be within a range of about 130-150 GPa.

The average microhardnesses of the resulting hot-pressed material was determined as follows. Pieces of the hot-pressed material (about 2 to 5 millimiters in size) were mounted in mounting resin (obtained under the trade designation “EPOMET” from Buehler Ltd., Lake Bluff, Ill.). The resulting cylinder of resin was about 2.5 cm (1 inch) in diameter and about 1.9 cm (0.75 inch) tall (i.e., high). The mounted samples were polished using a conventional grinder/polisher (obtained under the trade designation “EPOMET” from Buehler Ltd.) and conventional diamond slurries with the final polishing step using a 1-micrometer diamond slurry (obtained under the trade designation “METADI” from Buehler Ltd.) to obtain polished cross-sections of the sample.

The microhardness measurements were made using a conventional microhardness tester (obtained under the trade designation “MITLTOYO MVK-VL” from Mitutoyo Corporation, Tokyo, Japan) fitted with a Vickers indenter using a 500-gram indent load. The microhardness measurements were made according to the guidelines stated in ASTM Test Method E384 Test Methods for Microhardness of Materials (1991), the disclosure of which is incorporated herein by reference. The microhardness values were an average of 20 measurements. The average microhardness of the hot-pressed material was about 8.3 GPa.

The average indentation toughness of the hot-pressed material was calculated by measuring the crack lengths extending from the apices of the vickers indents made using a 500 g load with a microhardness tester (obtained under the trade designation “MITUTOYO MVK-VL” from Mitutoyo Corporation, Tokyo, Japan). Indentation toughness (KIC) was calculated according to the equation: K _(IC)=0.016 (E/H)^(1/2)(P/c)^(3/2) wherein:

-   -   E=Young's Modulus of the material;     -   H=Vickers hardness;     -   P=Newtons of force on the indenter;     -   c=Length of the crack from the center of the indent to its end.

Samples for the toughness were prepared as described above for the microhardness test. The reported indentation toughness values are an average of 5 measurements. Crack (c) were measured with a digital caliper on photomicrographs taken using a scanning electron microscope (“JEOL SEM” (Model JSM 6400)). The average indentation toughness of the hot-pressed material was 1.4 MPa·m^(1/2).

The thermal expansion coefficient of the hot-pressed material was measured using a thermal analyser (obtained from Perkin Elmer, Shelton, Conn., under the trade designation “PERKIN ELMER THERMAL ANALYSER”). The average thermal expansion coefficient was 7.6×10⁻⁶/° C.

The thermal conductivity of the hot-pressed material was measured according to an ASTM Standard “D 5470-95, Test Method A” (1995), the disclosure of which is incorporated herein by reference. The average thermal conductivity was 1.15 W/m·K.

The translucent disk of hot-pressed La₂O₃—Al₂O₃—ZrO₂ glass was heat-treated in a furnace (an electrically heated furnace (obtained under the trade designation “Model KKSK-666-3100” from Keith Furnaces of Pico Rivera, Calif.)) as follows. The disk was first heated from room temperature (about 25° C.) to about 900° C. at a rate of about 10° C./min and then held at 900° C. for about 1 hour. Next, the disk was heated from about 900° C. to about 1300° C. at a rate of about 10° C./min and then held at 1300° C. for about 1 hour, before cooling back to room temperature by turning off the furnace. Additional run was performed as described above except the final temperature was 1400° C.

FIG. 2 (a,b) is a scanning electron microscope (SEM) photomicrograph of a polished section of Example 1 materials heat-treated at 1300° C. and 1400° C., respectively, showing the fine crystalline nature of the material and the influence of the processing conditions on the crystallinity of the product. The polished section was prepared using conventional mounting and polishing techniques.

Based on powder x-ray diffraction of a portion of heat-treated Example 1 material and examination of the polished sample using SEM in the backscattered mode, it is believed that the dark portions in the photomicrograph were crystalline LaAl₁₁O₁₈, the gray portions crystalline LaAlO₃, and the white portions crystalline cubic/tetragonal ZrO₂ The Young's Modulus (E) of the heat-treated material was measured using an ultrasonic test system (obtained from Nortek, Richland, Wash., under the trade designation “NDT-140”), and found to be about 260 GPa. The average microhardness of the heat-treated at 1300° C. material was determined as described above was found to be 18.3 GPa. The average fracture toughness (K_(Ic)) of the heat-treated at 1300° C. material was determined as described above and was found to be 3.4 Mpa·m^(1/2).

The average microhardness of the heat-treated at 1400° C. material was determined to be 15.4 GPa. The average fracture toughness (K_(Ic)) of the heat-treated at 1400° C. material was determined to be 5.7 Mpa·m^(1/2).

The crush strength was measured for 90-125 micron amorphous beads according to the test procedure described in U.S. Pat. No. 4,772,511 (Wood et al.). (See Table I for crystallization conditions.) For comparison purposes, the crush strength of YTZ (yttria tetragonal zirconia) crystalline beads (100 microns in size) obtained from Tosoh Ceramics was also measured. Table I demonstrates the superior strength of beaded glass-ceramic materials of this invention compared to ZrO₂. TABLE I Crush Strength of Beaded Glass-ceramic Materials of the Invention Material Heat-treatment, ° C. Appearance Crush-strength, MPa Example 1 1225 Hazy/Clear 1601 Example 1 1300 Opaque 2282 ZrO₂ (“YTZ”) None Opaque 1234

Examples 2-62

Examples 2-62 beads were prepared as described in Example 1, except the raw materials and the amounts used are listed in Table II, below, and milling of raw materials was carried out in 90 ml of isopropyl alcohol with 200 g of the zirconia media (obtained from Tosoh Ceramics, Division of Bound Brook, N.J., under “YTZ” designation) at 120 rpm for 24 hours. TABLE II Bead Formulations Weight Percent of Powder Batch Example Components Amounts, g 2 La₂O₃: 45.06 La₂O₃: 22.53 Al₂O₃: 34.98 Al₂O₃: 17.49 ZrO₂: 19.96 ZrO₂: 9.98 3 La₂O₃: 42.29 La₂O₃: 21.15 Al₂O₃: 38.98 Al₂O₃: 19.49 ZrO₂: 8.73 ZrO₂: 9.37 4 La₂O₃: 39.51 La₂O₃: 19.76 Al₂O₃: 42.98 Al₂O₃: 21.49 ZrO₂: 17.51 ZrO₂: 8.76 5 La₂O₃: 36.74 La₂O₃: 18.37 Al₂O₃: 46.98 Al₂O₃: 23.49 ZrO₂: 16.28 ZrO₂: 8.14 6 La₂O₃: 38.65 La₂O₃: 19.33 Al₂O₃: 38.73 Al₂O₃: 19.37 ZrO₂: 22.62 ZrO₂: 11.31 7 La₂O₃: 40.15 La₂O₃: 20.08 Al₂O₃: 40.23 Al₂O₃: 20.12 ZrO₂: 19.62 ZrO₂: 9.81 8 La₂O₃: 43.15 La₂O₃: 21.58 Al₂O₃: 43.23 Al₂O₃: 21.62 ZrO₂: 13.62 ZrO₂: 6.81 9 La₂O₃: 35.35 La₂O₃: 17.68 Al₂O₃: 48.98 Al₂O₃: 24.49 ZrO₂: 15.66 ZrO₂: 7.83 10 La₂O₃: 32.58 La₂O₃: 16.20 Al₂O₃: 52.98 Al₂O₃: 26.49 ZrO₂: 14.44 ZrO₂: 7.22 11 La₂O₃: 31.20 La₂O₃: 15.60 Al₂O₃: 54.98 Al₂O₃: 27.49 ZrO₂: 13.82 ZrO₂: 6.91 12 La₂O₃: 28.43 La₂O₃: 14.22 Al₂O₃: 58.98 Al₂O₃: 29.49 ZrO₂: 12.59 ZrO₂: 6.30 13 La₂O₃: 26.67 La₂O₃: 13.34 Al₂O₃: 55.33 Al₂O₃: 27.67 ZrO₂: 18.00 ZrO₂: 9.00 14 ZrO₂: 5.00 ZrO₂: 2.50 La₂O₃: 86.50 La₂O₃: 43.25 Al₂O₃: 8.50 Al₂O₃: 4.25 15 ZrO₂: 10.00 ZrO₂: 5.00 La₂O₃: 81.90 La₂O₃: 40.95 Al₂O₃: 8.10 Al₂O₃: 4.05 16 CeO₂: 41.40 CeO₂: 20.70 Al₂O₃: 40.60 Al₂O₃: 20.30 ZrO₂: 18.00 ZrO₂: 9.00 17 Al₂O₃: 41.00 Al₂O₃: 20.50 ZrO₂: 17.00 ZrO₂: 8.50 Eu₂O₃: 41.00 Eu₂O₃: 20.50 18 Al₂O₃: 41.00 Al₂O₃: 20.50 ZrO₂: 18.00 ZrO₂: 9.00 Gd₂O₃: 41.00 Gd₂O₃: 20.50 19 Al₂O₃: 41.00 Al₂O₃: 20.50 ZrO₂: 18.00 ZrO₂: 9.00 Dy₂O₃: 41.00 Dy₂O₃: 20.50 20 Al₂O₃: 40.90 Al₂O₃: 20.45 Er₂O₃: 40.90 Er₂O₃: 20.45 ZrO₂: 18.20 ZrO₂: 9.10 21 La₂O₃: 35.00 La₂O₃: 17.50 Al₂O₃: 40.98 Al₂O₃: 20.49 ZrO₂: 18.12 ZrO₂: 9.06 Nd₂O₃: 5.00 Nd₂O₃: 2.50 22 La₂O₃: 35.00 La₂O₃: 17.50 Al₂O₃: 40.98 Al₂O₃: 20.49 ZrO₂: 18.12 ZrO₂: 9.06 CeO₂: 5.00 CeO₂: 2.50 23 La₂O₃: 35.00 La₂O₃: 17.50 Al₂O₃: 40.98 Al₂O₃: 20.49 ZrO₂: 18.12 ZrO₂: 9.06 Eu₂O₃: 5.00 Eu₂O₃: 2.50 24 La₂O₃: 35.00 La₂O₃: 17.50 Al₂O₃: 40.98 Al₂O₃: 20.49 ZrO₂: 18.12 ZrO₂: 9.06 Er₂O₃: 5.00 Er₂O₃: 2.50 25 HfO₂: 35.50 HfO₂: 17.75 Al₂O₃: 32.50 Al₂O₃: 16.25 La₂O₃: 32.50 La₂O₃: 16.25 26 La₂O₃: 41.7 La₂O₃: 20.85 Al₂O₃: 35.4 Al₂O₃: 17.70 ZrO₂: 16.9 ZrO₂: 8.45 MgO: 6.0 MgO: 3.00 27 La₂O₃: 39.90 La₂O₃: 19.95 Al₂O₃: 33.90 Al₂O₃: 16.95 ZrO₂: 16.20 ZrO₂: 8.10 MgO: 10.00 MgO: 5.00 28 La₂O₃: 43.02 La₂O₃: 21.51 Al₂O₃: 36.50 Al₂O₃: 18.25 ZrO₂: 17.46 ZrO₂: 8.73 Li₂CO₃: 3.00 Li₂CO₃: 1.50 29 La₂O₃: 41.70 La₂O₃: 20.85 Al₂O₃: 35.40 Al₂O₃: 17.70 ZrO₂: 16.90 ZrO₂: 8.45 Li₂CO₃: 6.00 Li₂CO₃: 3.00 30 La₂O₃: 38.80 La₂O₃: 19.40 Al₂O₃: 40.70 Al₂O₃: 20.35 ZrO₂: 17.50 ZrO₂: 8.75 Li₂CO₃: 3.00 Li₂CO₃: 1.50 31 La₂O₃: 43.02 La₂O₃: 21.51 Al₂O₃: 36.50 Al₂O₃: 18.25 ZrO₂: 17.46 ZrO₂: 8.73 TiO₂: 3.00 TiO₂: 1.50 32 La₂O₃: 43.02 La₂O₃: 21.51 Al₂O₃: 36.50 Al₂O₃: 18.25 ZrO₂: 17.46 ZrO₂: 8.73 NaHCO₃: 3.0 NaHCO₃: 1.50 33 La₂O₃: 42.36 La₂O₃: 21.18 Al₂O₃: 35.94 Al₂O₃: 17.97 ZrO₂ : 17.20 ZrO₂ : 8.60 NaHCO₃: 4.50 NaHCO₃: 2.25 34 La₂O₃: 43.02 La₂O₃: 21.51 Al₂O₃: 36.50 Al₂O₃: 18.25 ZrO₂ : 17.46 ZrO₂ : 8.73 MgO: 1.50 MgO: 0.75 NaHCO₃: 1.50 NaHCO₃: 0.75 TiO₂: 1.50 TiO₂: 0.75 35 La₂O₃: 43.00 La₂O₃: 21.50 Al₂O₃: 32.00 Al₂O₃: 16.0 ZrO₂: 12.00 ZrO₂: 6.00 SiO₂: 13.00 SiO₂: 6.50 36 Y₂O₃: 28.08 Y₂O₃: 14.04 Al₂O₃: 58.48 Al₂O₃: 29.24 ZrO₂: 13.44 ZrO₂: 6.72 37 Y₂O₃: 27.6 Y₂O₃: 13.80 Al₂O₃: 57.50 Al₂O₃: 23.75 ZrO₂: 14.90 ZrO₂: 7.45 38 Y₂O₃: 27.44 Y₂O₃: 13.72 Al₂O₃: 57.14 Al₂O₃: 28.57 ZrO₂: 15.43 ZrO₂: 7.71 39 Y₂O₃: 28.70 Y₂O₃: 14.35 Al₂O₃: 55.70 Al₂O₃: 27.85 ZrO₂: 15.50 ZrO₂: 7.75 40 Y₂O₃: 19.00 Y₂O₃: 9.50 Al₂O₃: 51.00 Al₂O₃: 25.50 ZrO₂: 17.90 ZrO₂: 8.95 La₂O₃: 12.10 La₂O₃: 6.05 41 Y₂O₃: 19.30 Y₂O₃: 9.65 Al₂O₃: 50.50 Al₂O₃: 25.25 ZrO₂: 17.80 ZrO₂: 8.90 Nd₂O₃: 12.40 Nd₂O₃: 6.20 42 Y₂O₃: 19.10 Y₂O₃: 9.55 Al₂O₃: 50 Al₂O₃: 25.00 ZrO₂: 17.80 ZrO₂: 8.90 Gd₂O₃: 13.10 Gd₂O₃: 6.55 43 Y₂O₃: 19.00 Y₂O₃: 9.50 Al₂O₃: 49.70 Al₂O₃: 24.85 ZrO₂: 17.55 ZrO₂: 8.77 Er₂O₃: 13.80 Er₂O₃: 6.90 44 Y₂O₃: 27.40 Y₂O₃: 13.70 Al₂O₃: 50.30 Al₂O₃: 25.15 ZrO₂: 17.80 ZrO₂: 8.90 Li₂CO₃: 4.50 Li₂CO₃: 2.25 45 HfO₂: 20.08 HfO₂: 14.04 Al₂O₃: 46.55 Al₂O₃: 23.27 Y₂O₃: 25.37 Y₂O₃: 12.67 46 Y₂O₃: 27.40 Y₂O₃: 13.7 Al₂O₃: 50.30 Al₂O₃: 25.15 ZrO₂: 17.80 ZrO₂: 8.90 MgO: 4.50 MgO: 2.25 47 Y₂O₃: 27.40 Y₂O₃: 13.70 Al₂O₃: 50.30 Al₂O₃: 25.15 ZrO₂: 17.80 ZrO₂: 8.90 CaO: 4.50 CaO: 2.25 48 Y₂O₃: 27.40 Y₂O₃: 13.70 Al₂O₃: 50.30 Al₂O₃: 25.15 ZrO₂: 17.80 ZrO₂: 8.90 TiO₂: 4.50 TiO₂: 2.25 49 Y₂O₃: 27.40 Y₂O₃: 13.70 Al₂O₃: 50.30 Al₂O₃: 25.15 ZrO₂: 17.80 ZrO₂: 8.90 NaHCO₃: 4.50 NaHCO₃: 2.25 50 Y₂O₃: 27.40 Y₂O₃: 13.70 Al₂O₃: 50.30 Al₂O₃: 25.15 ZrO₂: 17.80 ZrO₂: 8.90 SiO₂: 4.50 SiO₂: 2.25 51 Al₂O₃: 31.20 Al₂O₃: 15.60 La₂O₃: 34.00 La₂O₃: 17.00 ZrO2: 14.80 ZrO₂: 7.40 CaF₂: 20.00 CaF₂: 10.00 52 Al₂O₃: 35.73 Al₂O₃: 17.87 La₂O₃: 42.17 La₂O₃: 21.08 ZrO₂: 17.10 ZrO₂: 8.55 P₂O₅: 5.00 P₂O₅: 2.50 53 Al₂O₃: 35.73 Al₂O₃: 17.87 La₂O₃: 42.17 La₂O₃: 21.08 ZrO₂: 17.10 ZrO₂: 8.55 Nb₂O₅: 5.00 Nb₂O₅: 2.50 54 Al₂O₃: 35.73 Al₂O₃: 17.87 La₂O₃: 42.17 La₂O₃: 21.08 ZrO₂: 17.10 ZrO₂: 8.55 Ta₂O₅: 5.00 Ta₂O₅: 2.50 55 Al₂O₃: 35.73 Al₂O₃: 17.87 La₂O₃: 42.17 La₂O₃: 21.08 ZrO₂: 17.10 ZrO₂: 8.55 SrO: 5.00 SrO: 2.50 56 Al₂O₃: 35.73 Al₂O₃: 17.87 La₂O₃: 42.17 La₂O₃: 21.08 ZrO₂: 17.10 ZrO₂: 8.55 Mn₂O₃: 5.00 Mn₂O₃: 2.50 57 Al₂O₃: 36.50 Al₂O₃: 18.25 La₂O₃: 43.04 La₂O₃: 21.52 ZrO₂: 17.46 ZrO₂: 8.73 Fe₂O₃: 3.00 Fe₂O₃: 1.50 58 Al₂O₃: 36.50 Al₂O₃: 18.25 La₂O₃: 43.04 La₂O₃: 21.52 ZrO₂: 17.46 ZrO₂: 8.73 Cr₂O₃: 3.00 Cr₂O₃: 1.50 59 CaO: 36.00 CaO: 18.00 Al₂O₃: 44.00 Al₂O₃: 22.00 ZrO₂: 20.00 ZrO₂: 10.00 60 La₂O₃: 40.90 La₂O₃: 20.45 Al₂O₃: 40.98 Al₂O₃: 20.49 ZrO₂: 18.12 ZrO₂: 9.06 61 SrO: 22.95 SrO: 11.47 Al₂O₃: 62.05 Al₂O₃: 31.25 ZrO₂: 15.00 ZrO₂: 7.50 62 La₂O₃: 50.00 La₂O₃: 25.00 Al₂O₃: 22.00 Al₂O₃: 11.00 SiO₂: 28.00 SiO₂: 14.00

Various properties/characteristics of some Example 1-62 material were measured as follows. Powder x-ray diffraction (using an x-ray diffractometer (obtained under the trade designation “PHILLIPS XRG 3100” from PHILLIPS, Mahwah, N.J.) with copper K_(α1) radiation of 1.54050 Angstrom)) was used to qualitatively measure phases present in example materials. The presence of broad diffused intensity peak was taken as an indication of glassy nature of a material. The existence of both broad peak and well-defined peaks was taken as an indication of existence of crystalline matter within an amorphous matrix. Phases detected in various examples are reported in Table III, below. TABLE III Physical Characteristics of Beads of Examples 1-62 Glass Phases detected Transition Crystallization Hot-Pressing via x-ray Temperature Temperature Temperature Example diffraction Color (T_(g), ° C.) (T_(x), ° C.) (° C.) 1 Amorphous* Clear 834 932 960 2 Amorphous* Clear 837 936 960 3 Amorphous* Clear 831 935 — 4 Amorphous* Clear 843 928 — 5 Amorphous* Clear 848 920 960 6 Amorphous* Clear 850 923 — 7 Amorphous* Clear 849 930 — 8 Amorphous* Clear 843 932 — 9 Amorphous* Clear 856 918 960 10 Amorphous* Clear/milky 858 914 965 and crystalline 11 Amorphous* Clear/milky 859 914 — and crystalline 12 Amorphous* Clear/milky 862 912 — and crystalline 13 Amorphous* Clear/milky 875 908 — and crystalline 14 Crystalline and Milky/clear — — — amorphous 15 Crystalline and Milky/clear — — — amorphous 16 Amorphous* Brown 838 908 960 and crystalline 17 Amorphous* Intense 874 921 975 yellow/ mustard 18 Amorphous* Clear 886 933 985 19 Amorphous* Greenish 881 935 985 20 Amorphous* Intense pink 885 934 21 Amorphous* Blue/pink 836 930 965 fluorescent 22 Amorphous* Yellow 831 934 965 23 Amorphous* Yellow/gold 838 929 — 24 Amorphous* Pink 841 932 — 25 Amorphous* Light green 828 937 960 26 Amorphous* Clear 795 901 950 27 Amorphous* Clear 780 870 — 28 Amorphous* Clear 816 942 950 29 Amorphous* Clear 809 934 950 30 Amorphous* Clear/ 840 922 950 greenish 31 Amorphous* Clear 836 934 950 32 Amorphous* Clear 832 943 950 33 Amorphous* clear 830 943 950 34 Amorphous* Clear/some 818 931 950 green 35 Amorphous* Clear 837 1001  970 36 Amorphous* Clear/milky 874 932 980 and Crystalline 37 Amorphous* Clear/milky 871 934 — and Crystalline 38 Amorphous* Clear/milky 874 937 — and Crystalline 39 Amorphous* Clear/milky 870 942 — and Crystalline 40 Amorphous* Clear 843 938 970 41 Amorphous* Blue/pink 848 934 970 fluorescent 42 Amorphous* Clear/milky 880 943 — and Crystalline 43 Amorphous* Pink 876 936 — and Crystalline 44 Amorphous* Clear 821 927 970 45 Amorphous* Clear/ 867 948 — and Greenish Crystalline 46 Amorphous* Clear/milky 869 934 — and Crystalline 47 Amorphous* Clear 845 922 970 48 Amorphous* Clear/milky 870 933 — and Crystalline 49 Amorphous* Clear 831 916 970 50 Amorphous* Clear 826 926 970 51 Amorphous* Clear — 676 — 52 Amorphous* Clear 857 932 — 53 Amorphous* Clear — — — 54 Amorphous* Clear — — — 55 Amorphous* Clear — — — 56 Amorphous* Clear/Brown — — — 57 Amorphous* Clear/grey — — — 58 Amorphous* Clear/Green — — — 59 Amorphous* Clear 851 977 975 60 Amorphous* Clear 839 932 965 61 Amorphous* Clear 875 934 975 62 Amorphous* Clear 842 1085   1050** *glass, as the example has a T_(g) **sintering conducted without application of pressure

For differential thermal analysis (DTA), a material was screened to retain amorphous beads (microspheres) in the 90-125 micrometer size range. DTA runs were made (using an instrument obtained from Netzsch Instruments, Selb, Germany, under the trade designation “NETZSCH STA 409 DTA/TGA”). The amount of each screened sample placed in the 100 microliter Al₂O₃ sample holder was 400 milligrams. Each sample was heated in static air at a rate of 10° C./minute from room temperature (about 25° C.) to 1200° C.

Referring to FIG. 3, line 801 is the plotted DTA data for the Example 1 material. Referring to FIG. 3, line 801, the material exhibited an endothermic event at temperature around 840° C., as evidenced by the downward curve of line 801. It was believed that event was due to the glass transition (T_(g)) of the material. At about 934° C., an exothermic event was observed as evidenced by the sharp peak in line 801. It was believed that event was due to the crystallization (T_(x)) of the material. These T_(g) and T_(x) values for other examples are reported in Table III, above. The hot-pressing temperature at which appreciable glass flow occurred, as indicated by the displacement control unit of the hot pressing equipment described above, are reported for various examples in Table III, above. (In example 63, pressureless sintering was used.)

Example 63

About 120 g of the amorphous beads prepared as in Example 1 were placed in a graphite die and hot-pressed using uniaxial pressing apparatus (obtained under the trade designation “HP-50”, Thermal Technology Inc., Brea, Calif.). The hot-pressing was carried out at 960° C. in argon atmosphere and 2 ksi (13.8 MPa) pressure to provide a hot-pressed disk. Holding time at pressure was 30 minutes.

Two cylinders were core-drilled from the hot-pressed disk and mounted on CEREC-compatible stubs; one was approximately 12 mm in diameter×15 mm in height; the other was approximately 14 mm in diameter and 17 mm in height. The lanthanum oxide/aluminum oxide/zirconium oxide material was amorphous (glassy) and dark blue in color.

A dental coping was milled from the small cylinder on an automated milling system (available from Sirona Dental Systems, Bensheim, Germany, under the trade designation “CEREC 2”) with LS (LabSide) software; “CEREC 2” employs a 30 mm diameter metal-plated-diamond wheel and a 1.6 mm diameter cylindrical bur. Fresh tools and lubricant water were used. The restoration was milled in under 20 minutes, and appeared similar in form to the same restoration milled in a commercial block material, PARADIGM MZ100 Block for CEREC (available from 3M Company, St. Paul, Minn.) see FIG. 4.

Example 64

A billet (approximately 37 mm in diameter and 17 mm in height) of hot-pressed lanthanum oxide/aluminum oxide/zirconium oxide material was prepared as in Example 64; a 14 mm diameter×17 mm height cylinder was core-drilled from the billlet, then prepared for the CEREC by bonding it to a CEREC stub with an epoxy adhesive (available from 3M Company, St. Paul, Minn., under the trade designation “3M DP100”).

A molar full-occlusion crown was milled from the larger cylinder on the CEREC 3; a new diamond cone and 1.6-mm cylinder tools, and 100 ml of ProCAD DENTATEC Milling Additive (available from Sirona Dental Systems) in the water tank were used. The milled surface appeared identical to those of a commercial porcelain. The buccal surface was polished with a finishing brush (available from 3M Company, under the tradename, “SOF-LEX”). The resulting surface was smooth and suitable for occlusal contact.

Example 65

About 120 g of the amorphous beads prepared as in Example 1 were placed in a graphite die and hot-pressed using uniaxial pressing apparatus (obtained under the trade designation “HP-50”, Thermal Technology Inc., Brea, Calif.). The hot-pressing was carried out at 960° C. in argon atmosphere and 4 ksi (27.6 MPa) pressure. Holding time at pressure was 20 minutes. The resulting disk was core drilled to make five cylindrical specimens for dental milling evaluations.

Example 66

About 50 g of the amorphous beads prepared as in Example 1 were placed in a graphite die and hot-pressed using uniaxial pressing apparatus (obtained under the trade designation “HP-50”, Thermal Technology Inc., Brea, Calif.). The hot-pressing was carried out at 925° C. in argon atmosphere and 0.55 ksi (3.8 MPa) pressure. Holding time at pressure was 20 minutes. The resulting disk was core drilled to make one cylindrical specimen (approximately 10 mm in diameter×15 mm in height) for dental milling evaluations. The lanthanum oxide/aluminum oxide/zirconium oxide material was amorphous (glassy) and light yellow exhibiting some opalescence.

The block was bonded to a CEREC-compatible stub, and then machined on a CEREC 3 system (Sirona Dental Systems, Bensheim, Germany) using the set of diamond burs used in Example 65, and 75 ml of Sirona ProCAD DENTATEC lubricant in a fresh tank of deionized water. 1×4×12 mm bars were machined from the blocks. Visual inspection and the lack of error messages from the CEREC software indicated that the tools were capable of further machining. Examples 65 and 66 demonstrate that the material can be machined.

The thermal expansion behavior of Example 67 material was measured on a Seiko Thermomechanical Analyzer at a heating rate of 10° C./min. The coefficient of thermal expansion was 10.3 ppm/° C.; the softening point was about 880° C. A 10×10×3 mm disk of Example 66 material was heat-treated in a furnace (an electrically heated furnace (obtained under the trade designation “Model KKSK-666-3100” from Keith Furnaces of Pico Rivera, Calif.)) as follows. The disk was first heated from room temperature (about 25° C.) to about 900° C. at a rate of about 10° C./min and then held at 900° C. for about 1 hour. Next, the disk was heated from about 900° C. to about 1300° C. at a rate of about 10° C./min and then held at 1300° C. for about 1 hour, before cooling back to room temperature by turning off the furnace. Dimensional shrinkage that occurred during this heat-treatment was measured to be 4.5%.

Example 67

About 150 g of the amorphous beads prepared as described in Example 1 were placed in a 5 centimeter (cm)×5 cm×5 cm steel can, which was then evacuated and sealed from the atmosphere. The steel can was subsequently hot-isostatically pressed (HIPed) using a HIP apparatus (obtained under the trade designation “IPS Eagle-6”, American Isostatic Presses Inc., Ohio). The HIPing was carried out at 207 MPa (30 ksi) pressure in an argon atmosphere. The HIPing furnace was ramped up to 970° C. at 25° C./minute and held at that temperature for 30 minutes. After the HIPing, the steel can was cut and the charge material removed. It was observed that amorphous beads had coalesced into a dense body of transparent, glassy material. The DTA trace, conducted as summarized in Examples 2-62, exhibited a glass transition (T_(g)) of 879° C. and a crystallization temperature (T_(x)) of 931° C.

Example 68

35 g of amorphous beads from Example 1, and 15 g of α-Al₂O₃ (obtained from Condea Vista, Tucson, Ariz., under the trade designation “APA-0.5”), were placed in a polyethylene bottle. After 80 g of distilled water and 300 g of zirconia media (Tosoh Ceramics, Bound Brook, N.J., under the trade designation “YTZ”) was added to the bottle. The mixture was comminuted for 24 hours at 120 rpms. The milled material was dried using a heat gun. 20 g of the dried powder was hot-pressed as described in Example 1. The result was an opaque billet.

Example 69

20 g of amorphous beads prepared as described in Example 62, and 15 g of amorphous beads prepared as described in Example 1, were placed in an alumina crucible and heat-treated in a furnace (an electrically heated furnace (obtained under the trade designation “Model KKSK-666-3100”, from Keith Furnaces of Pico Rivera, Calif.)) at 1050° C. for 1 hour. The obtained material was translucent body with beads of Example 1 evenly distributed through an amorphous matrix of viscously flowed amorphous beads of Example 62.

Example 70

15 g of amorphous beads prepared as described in Example 1 were placed in an alumina crucible and heat-treated in a furnace (an electrically heated furnace (obtained under the trade designation “Model KKSK-666-3100” from Keith Furnaces of Pico Rivera, Calif.)) at 1250° C. for 4 hours. The obtained material was easily friable but handleable body.

A 1.4 g portion of this porous, bisque-fired body was placed onto a platinum foil; 0.6 g of a lanthana-alumina-silica glass powder (VITA IN-CERAM Alumina Infiltration Glass, shade A11: Vita Zahnfabrik H. Rauter GmbH & Co. KG) was placed on top of the body. The foil, body, and glass powder were then fired in a dental porcelain furnace under vacuum at 1120° C. for 60 minutes. After firing, the body was partially infiltrated with the glass; an additional 0.93 g of glass powder was placed on the body, and then fired again per the same condition. The resulting body was fully infiltrated with the glass.

A 5×5×5 mm (0.04 g) portion of the porous, bisque-fired body was partially immersed in a tray of photocurable resin (made by mixing 20.79 parts by weight bis-GMA, 29.11 parts UDMA, 29.11 parts Bis-EMA6, 4.16 parts TEGDMA, 14.00 parts HEMA, 0.172 parts CPQ, 0.43 parts DPIHFP, 0.86 parts EDMAB, 0.086 parts BHT and 1.29 parts NORBLOC 7966). After two hours, the resin was fully infiltrated into the block. The block was removed and cured by exposure to light from a 3M Company XL3000 Light Cure Unit for 10 seconds, followed by two 90 second cycles in a Kulzer Dentacolor XS unit (Kulzer, Wehrheim, Germany). The result was a hard, strong, resin-ceramic composite with two interpenetrating phases.

Example 71 Plasma-Spraying

A 250-ml polyethylene bottle (7.3-cm diameter) was charged with the following 50-gram mixture: 19.3 g of alumina particles (obtained from Alcoa Industrial Chemicals, Bauxite, Ark., under the trade designation “Al6SG”), 9.5 g of zirconium oxide particles (obtained from Zirconia Sales, Inc., of Marietta, Ga. under the trade designation “DK-2”), and 21.2 g of lanthanum oxide particles (obtained from Molycorp Inc., Mountain Pass, Calif.), 75 g of isopropyl alcohol, and 200 g of alumina milling media (cylindrical in shape, both height and diameter of 0.635 cm; 99.9% alumina; obtained from Coors, Golden, Colo.). The contents of the polyethylene bottle were milled for 16 hours at 60 revolutions per minute (rpm). The ratio of alumina to zirconia in the starting material was 2:1, and the alumina and zirconia collectively made up about 58 weight percent (wt-%). After the milling, the milling media were removed and the slurry was poured onto a warm (approximately 75° C.) glass (“PYREX”) pan and dried. The dried mixture was screened through a 70-mesh screen (212-micrometer opening size) with the aid of a paint brush.

After grinding and screening, the mixture of milled feed particles was fed slowly (0.5 gram/minute) into a hydrogen/oxygen torch flame to melt the particles and generate glass beads as described in Example 1. The glass beads were spherical in shape and varied in size from a few micrometers (i.e., microns) up to 250 micrometers. Subsequently, the flame-formed beads having diameters less than 125 micrometers were then passed through a plasma gun and deposited on stainless steel substrates as follows.

Four 304 stainless steel pieces (76.2 millimeter (mm)×25.4 mm×3.175 mm dimensions), and two 1080 carbon steel pieces (76.2 mm×25.4 mm×1.15 mm) were treated in the following manner. The sides to be coated were sandblasted, washed in an ultrasonic bath, and then wiped clean with isopropyl alcohol. The four 304 stainless steel and one of the 1080 carbon steel substrates were placed approximately 10 centimeters (cm) in front of the nozzle of a plasma gun (obtained under the trade designation “Praxair SG-100 Plasma Gun” from Praxair Surface Technologies, Concord, N.H.). The second 1080 carbon steel substrate was placed 18 cm in front of the nozzle of the plasma gun. The coatings made on the second 1080 carbon steel sample at a distance of 18 cm in front of the nozzle of the plasma gun were not further characterized.

The plasma unit had a power rating of 40 kW. The plasma gas was argon (50 pounds per square inch (psi), 0.3 megapascal (MPa)) with helium as the auxiliary gas (150 psi, 1 MPa). The beads were passed through the plasma gun by using argon as the carrier gas (50 psi, 0.3 MPa) using a Praxair Model 1270 computerized powder feeder (obtained from Praxair Surface Technologies, Concord, N.H.). During deposition, a potential of about 40 volts and a current of about 900 amperes was applied and the plasma gun was panned left to right, up and down, to evenly coat the substrates. When the desired thickness was achieved, the plasma spray was shut off and the samples were recovered. The 1080 carbon steel substrate was flexed, thus separating the coating from the substrate resulting in a free-standing bulk material. The deposited material had a z dimension (thickness) of about 1350 micrometers, as determined using optical microscopy.

The phase composition (glassy/amorphous/crystalline) was determined through Differential Thermal Analysis (DTA) as described below. The material was classified as amorphous if the corresponding DTA trace of the material contained an exothermic crystallization event (T_(x)). If the same trace also contained an endothermic event (T_(g)) at a temperature lower than T_(x), it was considered to consist of a glass phase. If the DTA trace of the material contained no such events, it was considered to contain crystalline phases.

Differential thermal analysis (DTA) was conducted using the following method. DTA runs were made (using an instrument obtained from Netzsch Instruments, Selb, Germany, under the trade designation “NETZSCH STA 409 DTA/TGA”) using a 140+170 mesh size fraction (i.e., the fraction collected between 105-micrometer opening size and 90-micrometer opening size screens). The amount of each screened sample placed in a 100-microliter Al₂O₃ sample holder was about 400 milligrams. Each sample was heated in static air at a rate of 10° C./minute from room temperature (about 25° C.) to 1100° C.

The coated material (on 304 stainless steel substrates) exhibited an endothermic event at a temperature around 880° C., as evidenced by a downward change in the curve of the trace. It is believed this event was due to the glass transition (T_(g)) of the glass material. The same material exhibited an exothermic event at a temperature around 931° C., as evidenced by a sharp peak in the trace. It is believed that this event was due to the crystallization (T_(x)) of the material. Thus, the coated material (on 304 stainless steel substrates) and the free-standing bulk material were glassy as determined by a DTA trace.

A portion of the glassy free-standing bulk material was then heat-treated at 1300° C. for 48 hours. Powder x-ray diffraction, XRD, (using an x-ray diffractometer (obtained under the trade designation “PHILLIPS XRG 3100” from Phillips, Mahwah, N.J.) with copper K_(α1) radiation of 1.54050 Angstrom)) was used to determine the phases present. The phases were determined by comparing the peaks present in the XRD trace of the crystallized material to XRD patterns of crystalline phases provided in JCPDS (Joint Committee on Powder Diffraction Standards) databases, published by International Center for Diffraction Data. The resulting crystalline material included LaAlO₃, ZrO₂ (cubic, tetragonal), LaAl₁₁O₁₈, and transitional Al₂O₃ phases.

Another portion of the glassy free-standing bulk material was crystallized at 1300° C. for 1 hour in an electrically heated furnace (obtained from CM Furnaces, Bloomfield, N.J., under the trade designation “Rapid Temp Furnace”). The crystallized coating was crushed with a hammer into particles. The fraction that passed through a sieve with a 600-micrometer opening size but did not pass through a screen with 500-micrometer openings was cleaned of debris by washing in a sonic bath (obtained from Cole-Parmer, Vernon Hills, Ill., under the trade designation “8891”) for 15 minutes, dried at 100° C. A portion of the particles was mounted on a metal cylinder (3 cm in diameter and 2 cm high) using carbon tape. The mounted sample was sputter coated with a thin layer of gold-palladium and viewed using a JEOL scanning electron microscopy (SEM) (Model JSM 840A). The fractured surface was rough and no crystals coarser than 200 nanometers (nm) were observed via SEM.

Example 72

Feed particles were made as described in Example 71 using the following 50-gram mixture: 21.5 g of alumina particles (obtained from Alcoa Industrial Chemicals, Bauxite, Ark. under the trade designation “Al6SG”), 9 g of zirconium oxide particles (obtained from Zirconia Sales, Inc. of Marietta, Ga. under the trade designation “DK-2”), and 19.5 g of cerium oxide particles (obtained from Rhone-Poulence, France). The ratio of alumina to zirconia in the starting material was 2.4:1 and the alumina and zirconia collectively made up about 61 weight percent. Feed particles were flame-formed into beads (of a size that varied from a few micrometers up to 250 micrometers) as described in Example 71. Subsequently, the flame-formed beads having diameters between 180 micrometers and 250 micrometers were passed through a plasma gun and deposited on stainless and carbon steel substrates as described in Example 71.

The coated 1080 carbon steel substrates were flexed, thus separating the coating from the substrate resulting in a free-standing bulk material. The resulting bulk material had a z dimension (thickness) of about 700 micrometers, as determined using optical microscopy. The microstructure was also observed using optical microscopy. The material consisted of generally spherical and oblique crystalline particles, which were opaque, within a predominantly amorphous matrix, which was transparent. Amorphous material is typically transparent due to the lack of light scattering centers such as crystal boundaries, while the crystalline particles show a crystalline structure and are opaque due to light scattering effects. The crystalline phases, determined by powder XRD analysis as described in Examples 71, consisted of Zr_(0.4)Ce_(0.6)O₂ (cubic) and transitional Al₂O₃.

A second deposition experiment was carried out using the flame-formed beads having diameters less than 125 micrometers. The resulting coating had a z dimension (thickness) of about 1100 micrometers, as determined using optical microscopy. The microstructure was also observed using optical microscopy. This material had similar features (i.e., consisted of generally spherical and oblique crystalline particles within a predominantly amorphous matrix) to those of the material formed from beads having diameters between 180 micrometers and 250 micrometers. The crystalline phases, determined by XRD analysis as described in Example 71 consisted of Zr_(0.4)Ce_(0.6)O₂ (cubic) and transitional Al₂O₃.

Example 73

Feed particles were made as described in Example 71 using the following 50-gram mixture: 27.9 g of alumina particles (obtained from Alcoa Industrial Chemicals, Bauxite, Ark. under the trade designation “Al6SG”), 7.8 g of zirconium oxide particles (obtained from Zirconia Sales, Inc., Marietta, Ga. under the trade designation “DK-2”), and 14.3 g of yttrium oxide particles (obtained from H.C. Stark Newton, Mass.). The ratio of alumina to zirconia of initial starting materials was 3.5:1 and the alumina and zirconia collectively made up about 72 weight percent. The feed particles were then screened through a 30-mesh screen (600-micrometer opening size) and heat-treated at 1400° C. for 2 hours in an electrically heated furnace (obtained from CM Furnaces, Bloomfield, N.J., under the trade designation “Rapid Temp Furnace”). The heat-treated particles were further screened to separate out particles with diameters between 125 micrometers and 180 micrometers, which were then passed through a plasma gun and deposited on stainless steel substrates as described in Example 71.

The 1080 carbon steel substrate was flexed, thus separating the coating from the substrate resulting in a free-standing bulk material. The resulting bulk material had a z dimension (thickness) of about 700 micrometers, as determined using optical microscopy. The microstructure was observed using optical microscopy. This material consisted of generally crystalline opaque particles (which retained their original shapes) within a predominantly transparent, amorphous matrix. The crystalline phases, determined by powder XRD analysis as described in Example 71, consisted of Al₅Y₃O₁₂ and Y_(0.15)Zr_(0.85)O_(1.93).

Another portion of the free-standing bulk material was crystallized at 1300° C. for 1 hour and the fractured surface was sputter coated with a thin layer of gold-palladium and viewed using a JEOL SEM (Model JSM 840A), as described above in Example 71. The fractured surface was rough and no crystals coarser than 200 nm were observed.

Example 74

A thick coating consisting of various layers of the above three examples was plasma sprayed using feed particles produced in Examples 71-73. The first layer was coated as described in Example 72, the second as described in Example 71, and the third as described in Example 73.

The substrate was not sandblasted prior to coating so that it was removed easily by plying it apart by hand, resulting in a free-standing bulk material, approximately 75 millimeters (mm)×25 mm×7.5 mm. Cylindrical blocks were prepared by core-drilling through the thick coating.

The first layer had a z dimension (thickness) of approximately 2.5 mm, as determined using optical microscopy. The microstructure was observed using optical microscopy. This material had similar features to those of the material of Example 72 (i.e., consisted of generally spherical and opaque crystalline particles within a predominantly transparent, amorphous matrix). The second layer had a z dimension (thickness) of approximately 2 mm, as determined using optical microscopy. The microstructure was also observed using optical microscopy. This material had similar features to those of the material of Example 71 (i.e., was transparent suggesting it was amorphous). The third layer had a z dimension (thickness) of approximately 3 mm, as determined using optical microscopy. The microstructure was also observed using optical microscopy. This material had similar features to those of the material of Example 73 (i.e., it consisted of generally opaque crystalline particles (which retained their original shapes) within a predominantly transparent, amorphous matrix).

The blocks had bands of color ranging from dark umber to light beige. Two blocks (approximately 10 mm diameter×15 mm height) were bonded to CEREC-compatible stubs, then machined on a CEREC 3 system (Sirona Dental Systems, Bensheim Germany) using a new set of diamond burs and 75 ml of Sirona ProCAD Dentatec lubricant in a fresh tank of deionized water. A molar crown was machined from one block; a coping for a maxillary lateral was machined from the other. No problems were encountered in machining. The resulting units were well machined. This example demonstrates that a plasma-sprayed embodiment of the invention can be made and machined, and also a multicolored block can be made.

Example 75

Nanoparticulates of La₂O₃—Al₂O₃—ZrO₂ (LAZ) and CeO₂—Al₂O₃—ZrO₂ (CAZ) materials the compositions shown in Table IV were prepared according to the method disclosed in U.S. Pat. No. 5,958,361 (Laine et al). TABLE IV Material CeO₂ La₂O₃ Al₂O₃ ZrO₂ LAZ NA 42.50 38.75 18.75 CAZ 39.00 NA 43.00 18.00 Other processes such as those described in U.S. Pat. No. 5,075,090, (Lewis et al) and U.S. Pat. No. 5,358,695 (Helble et al) can also be used to produce particulates useful in this example.

Powder x-ray diffraction, XRD, (using an x-ray diffractometer (obtained under the trade designation “PHILLIPS XRG 3100” from Phillips, Mahwah, N.J.) with copper K_(α1) radiation of 1.54050 Angstrom) was used to determine the phases present. The phases were determined by comparing the peaks present in the XRD trace of the crystallized material to XRD patterns of crystalline phases provided in JCPDS (Joint Committee on Powder Diffraction Standards) databases, published by International Center for Diffraction Data. The resulting phases are reported in Table V. TABLE V XRD Analysis of Crystalline Phases Identified Phases/Relative Intensities La₂O₃—Al₂O₃—ZrO₂ (LAZ) Amorphous + LaAlO₃ (D_(app) = 580 Å)/ 100 + “La_(0.25)Zr_(0.75)O_(1.875)”/37 + transitional Al₂O₃/18 CeO₂—Al₂O₃—ZrO₂ “Zr_(0.4)Ce_(0.6)O₂” (cubic, a₀ ≈ 5.30 Å) (D_(app) = 240 Å)/100 + transitional Al₂O₃/6 + (possible CeAlO₃)/5

5.570 g of LAZ powder was treated with 5.570 g of a silane agent (3M Company RELY X Ceramic Primer), allowed to dry; 3.618 g of the resulting powder was then blended with 2.59 g of the photocurable resin made by blending 24.18 parts by weight of bis-GMA, 33.85 parts UDMA, 33.85 parts bis-EMA6, 4.84 parts TEGDMA, 0.2 parts CPQ, 0.5 parts DPHFP, 1.0 parts EDMAB, 0.1 parts BHT, and 1.5 parts of NORBLOCK 7966. The resulting composite was white in color and had viscosity and handling suitable for a flowable style dental composite. The composite was filled into a mold 2 mm deep by 5 mm diameter, in two increments of 1 mm, each cured for 60 seconds with a 3M Company XL3000 Dental Curing Light. The hardness of the cured composite was measured with a Barcol Hardness meter, models GYZJ-934-1 (Barber Coleman, Inc., Loves Park, Ill.). An average Barcol Hardness of 91±0.6 was measured on the top surface of the cured composite.

An intracoronal inlay on a molar tooth was prepared in a gypsum dental model. The composite was loaded into the preparation in several 1-mm increments, each cured for 60 seconds with a 3M Company XL3000 Dental Curing Light; in the final increment, occlusal anatomy was sculpted into the composite before curing. The resulting inlay was esthetic.

Example 76

84.9 g of aluminum formoacetate were charged to a Pyrex beaker, which was then placed on a hotplate/stirred with a Teflon-coated stir bar; 16.5 g of zirconyl acetate (Magnesium Elektron Inc.) were added under vigorous stirring to form a clear, slightly turbid sol, followed by 22.5 g of lanthanum nitrate (Johnson Matthey #12915, 99.9%). The ingredients blended readily to form a clear, slightly turbid, opalescent sol with no precipitates, gelation, or thickening, suitable for further processes such as flame-spraying, spray-drying, coating, spray pyrolysis, gelation/drying/calcinations, gelation/autoclaving, or controlled precipitation of particles. The sol was calculated to have a nominal yield of 20 g of oxide of composition La₂O₃ 42.3 wt-%, Al₂O₃ 39.2 wt-%, ZrO₂ 18.5 wt-%. 9.1 g of polyethylene glycol MW=400 (PEG₄₀₀: Union Carbide Carbowax, Sentry Grade) was added to the sol; a small vial of this PEG-doped sol was saved to observe stability. This sol was stable for 8 hours, but developed white gel precipitates after 24 hours. To the remaining sol was added 10.8 g of the liquid component of VITREMER CORE Restorative liquid (available from 3M Company, St. Paul, Minn.), which formed a soft solid mass in 3 hours. This soft solid mass was dried at 100° C./5 hrs. TG/DTA analysis of the dried material showed weight loss below about 500° C. due to water evaporation and pyrolysis of the organics and nitrates/acetates. Exotherm peaks at 208° C. and 372° C. are due to the pyrolysis. Surprisingly, there were no endotherms from crystallization up to as high as 1300° C.; the resulting powder was white. Samples of the dried sol were calcined at 550° C./4 hr and 850° C./4 hr; the results (Table VI) show a large amorphous portion, and some crystalline phases. TABLE VI XRD Results Description Identified Phases/Relative Intensities LAZ sol-gel, calcined at 550° C.; La₂O₂CO₃/100 + La₂CO₅/65 + Grey, granular powder amorphous LAZ sol-gel, calcined at 850° C.; La₂O₃/100 + La(OH)₃/52 + LaAlO₃/ Off-white, granular powder 48 + amorphous

2.90 g of the powder was treated with 2.9 g of a silane agent (3M Company RELYX Ceramic Primer), allowed to dry, and then blended with 2.9 g of photocurable resin (made by blending 24.18 parts by weight bis-GMA, 33.85 parts UDMA, 33.85 parts Bis-EMA6, 4.84 parts TEGDMA, 0.2 parts CPQ, 0.5 parts DPHFP, 1.0 parts EDMAB, 0.1 parts BHT and 1.5 parts NORBLOC 7966)). The resulting composite was ivory in color and had viscosity and handling suitable for a flowable style dental composite. The composite was filled into a mold 2 mm deep by 5 mm diameter, in two increments of 1 mm, each cured for 60 seconds with a 3M Company XL3000 Dental Curing Light. The hardness of the cured composite was measured with a Barcol Hardness meter, models GYZJ-934-1 (Barber Coleman, Inc., Loves Park, Ill.). An average Barcol Hardness of 91+1 was measured on the top surface of the cured composite.

Example 77

42.6 parts by weight (pbs) of aluminum formoacetate were charged to a Pyrex beaker, which was then placed on a hotplate/stirred with a Teflon-coated stir bar; 8.3 pbw of zirconyl acetate (Magnesium Elektron Inc.) were added under vigorous stirring, followed by 11.3 pbw of lanthanum nitrate (Johnson Matthey #12915, 99.9%), then 0.6 pbw of polyethylene glycol MW=400 (PEG₄₀₀: Union Carbide Carbowax, Sentry Grade), and sufficient nitric acid to reduce the pH from ˜4.4 to ˜3-3.3. The ingredients blended readily to form a clear, slightly turbid, opalescent sol with no precipitates, gelation, or thickening, suitable for further processes such as flame-spraying, spray-drying, coating, spray pyrolysis, gelation/drying/calcinations, gelation/autoclaving, or controlled precipitation of particles. The sol was calculated to have a composition La₂O₃ 42.3 wt-%, Al₂O₃ 39.2 wt-%, ZrO₂ 18.5 wt-%. The sol was spray-dried immediately after mixing to a fine, free-flowing powder in a Buchi spray dryer. TG/DTA analysis of the dried material shows weight loss below circa 500° C. due to water evaporation and pyrolysis of the organics and nitrates/acetates. An exotherm peaks at 100.7° C. can be attributed to water evaporation, and 348.7° C. to the pyrolysis of the organics. Surprisingly, there are no endotherms from crystallization up to as high as 1300° C.; the resulting powder was white.

A small sample of an identically blended sol was retained to observe stability; another small sample was diluted with water by mixing 2.3 g of sol and 1.7 g deionized water. Both sols were stable at 15 hr; the undiluted sol developed a fine layer of white precipitate by circa 40 hours, while the diluted sol was free of precipitates, gelation, or thickening after 5 days.

A sample of this powder was calcined at 550° C. for 1 hour in air (resultant powder was white) and hot-pressed at 970° C. as described in Example 1; XRD on resulting semi-solid disk showed that the major crystalline phase present was a face-centered cubic (FCC) crystal structure with a lattice parameter of ˜5.28 Å, most likely due to a stabilized form of zirconia. A possible transitional alumina phase was also observed, as well as an unidentified phase(s) with diffraction peaks at d-spacings of ˜4.1 Å and ˜3.7 Å. The powder was then fired at 700° C./4 hr; the resulting white powder was crushed in a mortar and pestle.

Example 78

84.9 g of aluminum formoacetate were charged to a PYREX beaker, which was then placed on a hotplate/stirrer with a Teflon-coated stir bar; 16.6 g of zirconyl acetate were added under vigorous, followed by 87.3 g deionized water, 22.5 g of lanthanum nitrate hexahydrate, 1.8 g polyethylene glycol (MW=400), and 3.6 g nitric acid. The ingredients blended readily to form a clear, slightly turbid, opalescent sol with no precipitates, gelation, or thickening, suitable for further processes such as flame-spraying, spray-drying, coating, spray pyrolysis, or controlled precipitation. The sol was calculated to have a nominal yield of 42.3 wt-% La₂O₃, 39.2% Al₂O₃, and 18.5% ZrO₂.

The sol was applied to the following substrates with a cotton swab:

-   -   A. glass slide: 1 coat, dry in air     -   B. glass slide: 1 coat, dry with compressed air     -   C. glass slide: 4 coats, dried in air between coats     -   D. opaque aluminum oxide wafer: 1 coat, dry in air     -   E. translucent alumina wafer: 1 coat, dry in air     -   F. translucent alumina wafer: 1 coat, dry in air (thicker layer)     -   G. glass slide: swipe several lines, dry in air         The coated substrates were fired at 550° C./2 hr. Samples (B),         (E), (G) were clear and well-bonded; the others were black and         flaky. The remaining sol was stored under ambient storage         conditions in a sealed vial; after 13 days the sol remained free         of precipitates, gelation, separation, or thickening.

Example 79

The samples of Example 78 were additionally fired at 560° C. for 8 hours. On samples where the brushed sol coating was thick, the fired coating was dark brown and could be rubbed off; on samples where the brushed sol coating was thin (because of compressed air drying, or barely-wet brush), the coating was clear and well-bonded. The sol has been stable for 13 days to date, with no precipitates, gelation, or thickening.

The complete disclosures of the patents, patent documents, and publications cited herein are incorporated by reference in their entirety as if each were individually incorporated. Various modifications and alterations to this invention will become apparent to those skilled in the art and are foreseeable without departing from the scope and spirit of this invention. It should be understood that this invention is not intended to be unduly limited by the illustrative embodiments and examples set forth herein and that such examples and embodiments are presented by way of example only with the scope of the invention intended to be limited only by the claims set forth herein as follows. 

1. A method of making a dental article or orthodontic appliance comprising the steps of: plasma or thermally spraying particles comprising metal oxide sources onto a suitable substrate such that the particles coalesce to form a shaped article; and optionally separating the shaped article or appliance from the substrate, wherein the shaped article comprises at least one glass of: a) at least 35 percent by weight Al₂O₃, based on the total weight of the glass, and a first metal oxide other than Al₂O₃, wherein the glass contains not more than 10 percent by weight collectively B₂O₃, GeO₂, P₂O₅, SiO₂, TeO₂, and V₂O₅, based on the total weight of the glass; b) at least 35 percent by weight Al₂O₃, based on the total weight of the glass, and a first metal oxide other than Al₂O₃, wherein the Al₂O₃ and the first metal oxide collectively comprise at least 70 percent by weight of the glass; c) Al₂O₃ and at least one of REO or Y₂O₃, wherein at least 80 percent by weight of the glass collectively comprises the Al₂O₃ and the at least one of REO or Y₂O₃, based on the total weight of the glass; d) Al₂O₃, at least one of REO or Y₂O₃, and at least one of ZrO₂ or HfO₂, wherein at least 80 percent by weight of the glass collectively comprises the Al₂O₃, at least one of REO or Y₂O₃, and at least one of ZrO₂ or HfO₂, based on the total weight of the glass; e) Al₂O₃ and at least one of REO or Y₂O₃, wherein at least 60 percent by weight of the glass collectively comprises the Al₂O₃ and the at least one of REO or Y₂O₃, and wherein the glass contains not more than 20 percent by weight SiO₂ and not more than 20 percent by weight B₂O₃, based on the total weight of the glass; f) Al₂O₃, at least one of REO or Y₂O₃, and at least one of ZrO₂ or HfO₂, wherein at least 60 percent by weight of the glass collectively comprises the Al₂O₃, at least one of REO or Y₂O₃, and at least one of ZrO₂ or HfO₂, and wherein the glass contains not more than 20 percent by weight SiO₂ and not more than 20 percent by weight B₂O₃, based on the total weight of the glass; g) Al₂O₃ and at least one of REO or Y₂O₃, wherein at least 60 percent by weight of the glass comprise the Al₂O₃ and the at least one of REO or Y₂O₃, and wherein the glass contains not more than 40 percent by weight collectively SiO₂, B₂O₃, and P₂O₅, based on the total weight of the glass; or h) Al₂O₃, at least one of REO or Y₂O₃, and at least one of ZrO₂ or HfO₂, wherein at least 60 percent by weight of the glass collectively comprises the Al₂O₃, at least one of REO or Y₂O₃, and at least one of ZrO₂ or HfO₂, and wherein the glass contains not more than 40 percent by weight collectively SiO₂, B₂O₃, and P₂O₅, based on the total weight of the glass. 